Electroconductive laminate and touch panel using thereof

ABSTRACT

The present invention is an electroconductive laminate characterized in that the hard coat layer is formed from a hard coating composition which contains (A) a phenolic novolac acrylate having two or more acrylate groups, (B) a bisphenol structure-containing diacrylate having 2 to 4 moles of alkylene oxide structure with two or three carbon atoms in each molecule, (C) a polyfunctional acrylate having three or more acrylate groups, and (D) a polyfunctional urethane acrylate having three or more acrylate groups and an ester structure.

TECHNICAL FIELD

The present invention relates to an electroconductive laminate in which a hard coat layer and an electrically conducting layer are formed on at least one surface of a polycarbonate substrate, in particular, an electroconductive laminate having a hard coat layer that has stretchability in addition to high visibility and excellent hardness, while exhibiting excellent adhesion toward a polycarbonate substrate, and a touch panel using thereof.

BACKGROUND OF THE INVENTION

A liquid crystal display device has advantages such as thinness, lightweight, low power consumption and so on, and is widely used in various technical fields such as computers, word processors, television sets, mobile phones, handheld terminal devices and so on. In addition, so-called touch panels of such liquid crystal display devices having a mechanics of manipulation by touch on their screen are spreading rapidly. The touch panels are widely used in mobile phones like smart phones, tablet computers, handheld terminal devices, automated teller machines, automatic vending machines, personal digital assistances, copying machines, facsimiles, game machines, guiding devices set up in facilities such as museums and department stores, car navigation systems, multifunctional terminals set up in convenience stores or monitoring devices of railroad vehicles.

The touch panel generally has a transparent electroconductive laminate comprising a transparent substrate on which a transparent electrically conductive layer is formed. Indium tin oxide is generally used to form a transparent electrically conducting layer.

A PET film or a polycarbonate film is commonly used as a substrate film of a transparent electroconductive laminate thanks to its high transparency and reasonable prices. A transparent hard coat layer can be preferably applied onto such a substrate film with a view to improving scratch resistance and durability. On the other hand, the application of a transparent hard coat layer onto a substrate causes a problem of the appearance of interference fringes. The appearance of interference fringes deteriorates visibility.

As for the appearance of interference fringes, the inventors et al., have already found a hard coating composition in the patent application No. JP 2012-079755 or JP 2012-079756, which solves the problem by providing a layer having a refractive index close to a refractive index of a polycarbonate substrate. The above two patent applications were unpublished applications at the time of filing the earlier application given as the basis for the priority. On the other hand, the hard coating composition in the above two patent applications has required further improvements.

Above-mentioned patent applications include phenylphenol acrylate that is comprised as a component of a hard coat layer. This component is a mono-functional component having a low molecular weight. The inventors assume that such a component may improve an adhesion to the polycarbonate substrate which is often used as a substrate by an etching erosion of the polycarbonate substrate. However, such phenylphenol acrylate is a mono-functional component having a low molecular weight. Thus, when a pyrolysis is generated, it may become a volatile component and it tends to inhibit a crystallization of the transparent conductive film formed on the hard coat layer (typically an ITO film). As a result, in the production of an electroconductive laminate, workability is lowered. Also, the phenylphenol acrylate component may improve an adhesion between the polycarbonate substrate and the hard coat layer by the etching erosion of the polycarbonate substrate as described-above. But, a higher level of an adhesion test (severe adhesion test) will generate a problem that a cohesive failure of the substrate surface is generated.

PRIOR ART DOCUMENTS Patent Documents

Patent Document 1: JP patent application No. 2012-079755 (JP 2013-209481 A)

Patent Document 2: JP patent application No. 2012-079756 (JP 2013-209482 A)

SUMMARY OF THE INVENTION Problems to be Resolved by the Invention

The present invention has an object to resolve the above problems in the conventional technology. In details, the present invention has an object to improve a hard coat layer in an electroconductive laminate which the inventors et al, have been developed, to improve adhesion between a hard coat layer and a polycarbonate substrate, and to eliminate a volatile component so that the volatile component does not volatilize during heat treatment.

Means of Solving the Problems

The present invention provides the following embodiments, to solves the above problems.

[1]

The present invention relates to an electroconductive laminate in which a hard coat layer and an electrically conducting layer are formed on at least one surface of a polycarbonate substrate, wherein

the hard coat layer is obtained by a hard coating composition comprising

(A) a phenolic novolac acrylate having two or more acrylate groups,

(B) a bisphenol structure-containing diacrylate having 2 to 4 moles of alkylene oxide structure with two or three carbon atoms in each molecule,

(C) a polyfunctional acrylate having three or more acrylate groups, and

(D) a polyfunctional urethane acrylate having three or more acrylate groups and an ester structure, wherein

the hard coating composition comprises

15 to 25 parts by mass of the phenolic novolac acrylate (A),

25 to 35 parts by mass of the bisphenol structure-containing diacrylate (B),

25 to 35 parts by mass of the polyfunctional acrylate (C), and

15 to 25 parts by mass of the polyfunctional urethane acrylate (D), with respect to 100 parts by mass of a resin content in the hard coating composition, and wherein

the electroconductive laminate is substantially free of the resin component that may volatilize during a heat treatment of the electroconductive laminate carried out at 130° C. for 2 hours. Thereby, the above problem is solved.

[2]

The phenolic novolac acrylate (A) may preferably be represented by the following formula (I):

wherein R¹ represents H or CH₂OH, R² represents H or OH, n represents a number of 2 to 5 and m represents a number of 0 to 5. [3] The hard coat layer may preferably have a refractive index within a range of 1.535 to 1.545. [4] A total content of ZnO, TiO₂, CeO₂, SnO₂, ZrO₂ and indium tin oxide in the hard coat layer may preferably be less than or equal to 0.0001% by mass. [5] The electrically conducting layer may preferably have a thickness within a range of 5 to 100 nm. [6] The present invention also provides an electroconductive laminate in which a hard coat layer, a color difference adjusting layer, and an electrically conducting layer are formed on at least one surface of a polycarbonate substrate, wherein

the hard coat layer is obtained by a hard coating composition comprising

(A) a phenolic novolac acrylate having two or more acrylate groups,

(B) a bisphenol structure-containing diacrylate having 2 to 4 moles of alkylene oxide structure with two or three carbon atoms in each molecule,

(C) a polyfunctional acrylate having three or more acrylate groups, and

(D) a polyfunctional urethane acrylate having three or more acrylate groups and an ester structure, wherein

the hard coating composition comprises

15 to 25 parts by mass of the phenolic novolac acrylate (A),

25 to 35 parts by mass of the bisphenol structure-containing diacrylate (B),

25 to 35 parts by mass of the polyfunctional acrylate (C), and

15 to 25 parts by mass of the polyfunctional urethane acrylate (D), with respect to 100 parts by mass of a resin content in the hard coating composition, wherein

the electroconductive laminate is substantially free of the resin component that may volatilize during heat treatment of the electroconductive laminate carried out at 130° C. for 2 hours, wherein

the color difference adjusting layer is obtained by a composition comprising a curing resin component (i), and at least one of metal oxide particles having an average primary particle diameter of 100 nm or less (ii) and metal fluoride particles having an average primary particle diameter of 100 nm or less (iii), and

where a total mass of the particles (ii) and (iii) in the color difference adjusting layer is 0 to 200 parts by mass with respect to 100 parts by mass of the curing resin component (i), and wherein

a difference ΔR of R1 and R2 is equal to or less than 1, wherein R1 is a reflectance obtained by irradiation with a light source having a wavelength in a range of 500 to 750 nm toward the electroconductive laminate, and R2 is a reflectance obtained by irradiation with a light source having a wavelength in a range of 500 to 750 nm toward an electroconductive laminate after immersion into a strong acid aqueous solution at 40° C. for three minutes and dried, wherein the strong acid aqueous solution is obtained by a mixing of 12 N hydrochloric acid, 16 N nitric acid and water in a mass ratio of 12 N hydrochloric acid:16 N nitric acid:water being 3.3:1.0:7.6.

[7]

A total content of a sulfur-containing organic compound in the electroconductive laminate may preferably be within a range of 0 to 2000 ppm.

[8]

The electroconductive laminate has an auxiliary electrode layer that may preferably be formed on the electrically conducting layer, and wherein a total thickness of the electrically conducting layer and the auxiliary electrode layer is within a range of 20 to 500 nm. [9] The present invention relates to an electroconductive laminate in which a hard coat layer, a color difference adjusting layer, and an electrically conducting layer may be preferably formed on at least one surface of a polycarbonate substrate, and in which preferably

an anti-blocking layer obtained by a composition for forming an anti-blocking layer containing a first component and a second component is formed on another surface of the transparent polymer (polycarbonate) substrate, wherein

the first component contains an acrylic copolymer having an unsaturated double bond, the second component contains a polyfunctional acrylate,

a difference of SP values (ΔSP) of the first component (SP1) and the second component (SP2) is within a range of 1 to 2, and

the anti-blocking layer having a microscopic convexoconcave on its surface is obtained by a phase separation that occurs between the first component and the second component after the composition for forming an antiblocking layer is applied.

[10]

The present invention also provides a touch panel having an electrode substrate on which an electrically conductive layer is formed on at least one surface of the electrode substrate, wherein

the electroconductive laminate of the present application may preferably be used as at least one electrode substrate.

Advantageous Effect of the Invention

The electroconductive laminate according to the present invention has a hard coat layer obtained by applying a specific hard coating composition onto a polycarbonate substrate. The hard coat layer according to the present invention has features of excellent hardness, high visibility and stretchability. The hard coat layer according to the present invention also has a high refractive index. Therefore, the present invention has an advantage to prevent the occurrence of interference fringes in case that the hard coat layer according to the present invention is applied onto a high refractive index substrate film such as a polycarbonate film.

A resin components contained in the hard coating composition according to the present invention also has a technical characteristic of providing a high refractive index, even if the hard coating composition does not substantially include high refractive index materials such as metal oxide. The hard coat layer according to the present invention also has features of excellent stretchability, in addition to excellent hardness and high refractive index.

The hard coating composition which provides the hard coat layer according to the present invention does not contain a resin component that may volatilize due to heat or pressure applied in the process of manufacturing the touch panel electrode, or not comprise a resin component having a structure that may volatilize by degradation. Therefore, the present invention has an advantage that the inhibition of crystallization of the transparent electrically conductive layer formed on the upper layer is small. In addition, with regard to adhesion, adhesion to a polycarbonate substrate and a layer formed on the upper layer is improved together. Therefore, even in a higher level of an adhesion test (severe adhesion test), high adhesion can be ensured.

The hard coating composition for forming the hard coat layer of the present invention contains a urethane acrylate having an ester structure. Thus, as described-above, even in a higher level of the adhesion test (severe adhesion test), high adhesion can be ensured. The hard coat layer of the present invention also provides a technical effect that the occurrence of interference fringes is prevented, even in case that the hard coat layer is applied onto a polycarbonate substrate. In general, when difference in refractive index between a polycarbonate substrate and a hard coat layer is large, the occurrence of interference fringe is observed. However, the hard coating layer of the present invention provides a technical effect that the occurrence of interference fringes is prevented, even in case that the hard coat layer has a refractive index within a range of 1.535 to 1.545.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic explanatory view showing a transparent electroconductive laminate subjected to etching treatment.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The electroconductive laminate according to the present invention is an electroconductive laminate in which a hard coat layer, a color difference adjusting layer and an electrically conducting layer are formed on at least one surface of a polycarbonate substrate. The present invention includes an embodiment without a color difference adjusting layer. However, the present specification describes an embodiment with a color difference adjusting layer in view of conveniences. Also, an order of the layers according to the present invention is not limited in the above-mentioned order. However, the present specification describes the above-mentioned order in view of simplification of explanation. Furthermore, in many cases, the electroconductive laminate according to the present invention seems to be basically used as a transparent electroconductive laminate. However, an embodiment of the electroconductive laminate according to the present invention is not limited to a transparent electroconductive laminate. Therefore, the electroconductive laminate according to the present invention includes an embodiment having an opaque electrically conducting layer. Each layers constituting the electroconductive laminate according to the present invention is explained below.

Polycarbonate Substrate

A polycarbonate substrate used in the electroconductive laminate according to the present invention is generally a transparent substrate. However, a polycarbonate substrate is not necessarily a transparent because the electroconductive laminate according to the present invention is not limited to a transparent electroconductive laminate described above. In case that a polycarbonate substrate is a transparent, a substrate having less optical birefringence, a substrate having controlled phase difference such as one out of four (1/4) of a wavelength such as 550 nm, i.e., λ/4, or one out of two (1/2) of a wavelength, i.e., λ/2, or a substrate without controlled birefringence of the transparent polymer substrates can be selected in view of its use. The selection in view of its use includes, for example, using the transparent electroconductive laminate according to the present invention with a display which expresses a function by polarization such as linearly polarization, elliptic polarization or circular polarization, specifically, for example, a polarizing plate or a phase difference film used in a liquid-crystal display, and an inner-type touch panel.

A refractive index of a polycarbonate substrate may vary depending on its component monomer, and is generally in a range of about not less than 1.5 and less than 1.6. A phase difference R(550) of a polycarbonate film may preferably be in a range of 0 to 160 nm. A polycarbonate film may preferably satisfy the following formulae (1) and (2): 0.60<R(450)/R(550)<1.20  (1) 0.80<R(650)/R(550)<1.40  (2) (provided that R(450), R(550) and R(650) mean a phase difference in a film surface at a wavelength of 450 nm, 550 nm and 650 nm, respectively.) A refractive index of a polycarbonate substrate may more preferably be in a range of not less than 1.56 and less than 1.60. Most preferably, a polycarbonate film may has a refractive index of not less than 1.57 and less than 1.59, a phase difference R(550) is 0 to 10 nm and satisfy the following formulae (3) and (4): 1.01<R(450)/R(550)<1.20  (3) 0.80<R(650)/R(550)<0.99  (4)

A thickness of a polycarbonate substrate can be appropriately selected. The thickness may be 10 to 500 μm in view of its strength or handling property, preferably 20 to 300 μm, more preferably 30 to 200 μm.

Hard Coat Layer

The hard coat layer in the electroconductive laminate according to the present invention is hard coat layer which obtained by applying and curing a hard coating composition containing

(A) a phenolic novolac acrylate having two or more acrylate groups,

(B) a bisphenol structure-containing diacrylate having 2 to 4 moles of alkylene oxide structure with two or three carbon atoms in each molecule,

(C) a polyfunctional acrylate having three or more acrylate groups, and

(D) a polyfunctional urethane acrylate having three or more acrylate groups and an ester structure.

In the present invention, the hard coating composition necessarily contains;

15 to 25 parts by mass of the phenolic novolac acrylate (A),

25 to 35 parts by mass of the bisphenol structure-containing diacrylate (B),

25 to 35 parts by mass of the polyfunctional acrylate (C), and

15 to 25 parts by mass of the polyfunctional urethane acrylate (D), with respect to 100 parts by mass of a resin content in the hard coating composition.

(A) A Phenolic Novolac Acrylate Having Two or More Acrylate Groups

The hard coating composition contains (A) a phenolic novolac acrylate having two or more acrylate groups. The hard coating composition containing the phenolic novolac acrylate (A) can provide a high refractive index hard coat layer with transparency and excellent hardness. The technical feature can effectively prevent appearance of interference fringes.

The phenolic novolac acrylate (A) may preferably be represented by the following formula (I):

wherein R¹ represents H or CH₂OH, R² represents H or OH, n represents a number of 2 to 5 and m represents a number of 0 to 5.

In the above formula (I), n may preferably represent a number of 2 to 4 and m may preferably represent a number of 0 to 3, more preferably n may represent a number of 2 to 4 and m may represent a number of 0 to 1.

The phenolic novolac acrylate (A) may preferably have a weight average molecular weight of 400 to 2500, more preferably 450 to 2000. The phenolic novolac acrylate (A) may preferably have a hydroxyl value of 100 to 180 mgKOH/g, more preferably 120 to 160 mgKOH/g.

In this specification, weight average molecular weights of various components can be measured by gel permeation chromatography (GPC). In a measurement of weight average molecular weights, a high performance gel permeation chromatography apparatus such as HLC-8220GPC (manufactured by Tosoh Corporation) can be used. A concrete measurement condition of weight average molecular weights in use of HLC-8220GPC (manufactured by Tosoh Corporation) is, for example, measuring a test sample (2 g), drying the test sample in a vacuum dryer at 40° C. for 2 hours to remove a water, diluting the sample by THF solution in a concentration of 0.2%, then measuring under the following conditions: column injection amount of 10 μl, flow late of 0.35 ml/min.

The hard coating composition comprises 15 to 25 parts by mass of the phenolic novolac acrylate (A) providing that 100 parts by mass of a resin content in the hard coating composition. When an amount of the phenolic novolac acrylate (A) is less than 15 parts by mass, a hardness of the resulting hard coat layer may be lowered. When an amount of the phenolic novolac acrylate (A) is more than 25 parts by mass, there is disadvantage that an adhesion property toward a transparent polymer substrate such as a polycarbonate film becomes lower.

(B) A Bisphenol Structure-Containing Diacrylate Having 2 to 4 Moles of Alkylene Oxide Structure with Two or Three Carbon Atoms in Each Molecule

The hard coating composition according to the present invention contains (B) a bisphenol structure-containing diacrylate having 2 to 4 moles of alkylene oxide structure in each molecule. The acrylate (B) can provide wettability toward a polymer substrate such as a polycarbonate film, derived from a bisphenol structure thereof, which provides advantages of increasing of adhesion property of the hard coat layer. A concrete example of the acrylate (B) may include a reactant obtained by chain-extending of bisphenol F or bisphenol A with ethylene oxide, then reacting with (meth)acrylic acid.

A commercially available product may be used as the component (B). The commercially available product may include, for example,

Aronix M-208 (a bisphenol F EO-modified diacrylate (a number of ethylene oxide structure: about 4 mole in a molecular)) and Aronix M211B (a bisphenol A EO-modified diacrylate (a number of ethylene oxide structure: about 4 mole in a molecular)), produced by Toagosei co., ltd.; Light acrylate BP-4EAL (a bisphenol A EO-addition diacrylate, (a number of ethylene oxide structure: about 4 mole in a molecular)), produced by Kyoeisha Chemical co., ltd.; NK ester ABE-300 (an ethoxylated bisphenol A diacrylate, (a number of ethylene oxide structure: about 3 mole in a molecular) and A-BPE-4 (an ethoxylated bisphenol A diacrylate, (a number of ethylene oxide structure: about 4 mole in a molecular), produced by Shin-Nakamura Chemicals, co., ltd.); and the like.

In the present invention, the hard coating composition contains 25 to 35 parts by mass of the component (B) providing that 100 parts by mass of a resin content in the hard coating composition. When an amount of the component (B) is less than 25 parts by mass, adhesion property of the resulting hard coat layer toward a transparent polymer substrate such as a polycarbonate film becomes lower. When an amount of the component (B) is more than 35 parts by mass, there is disadvantages that refractive index of resulting hard coat layer becomes lower and poor visibility may be obtained.

(C) A Polyfunctional Acrylate Having Three or More Acrylate Groups

The hard coating composition according to the present invention contains a polyfunctional acrylate having three or more acrylate groups. The polyfunctional acrylate ordinarily has a molecular weight which is referred to as a monomer, it may be an oligomer in which two or more molecules are coupled. The polyfunctional acrylate monomer can cause a cure reaction due to a (meth) acryloyl group reaction, with an exposure to active energy rays after applying the hard coating composition. The cure reaction can provide a hard coat layer with excellent hardness, in which may be advantageous.

Such a polyfunctional acrylate having three or more acrylate groups includes, for example, hydroxypropylated trimethylolpropane triacrylate, pentaerythritol triacrylate, dipentaerythritol pentaacrylate, trimethylolpropane triacrylate, tris(acryloxyethyl) isocyanurate, ditrimethylolpropane tetraacrylate, pentaerythritol tetraacrylate, dipentaerythritol hexaacrylate and oligomers thereof. The polyfunctional acrylate may be used with alone or a combination of two or more.

The hard coating composition comprises 25 to 35 parts by mass of the component (C) providing that 100 parts by mass of a resin content in the hard coating composition. When an amount of the component (C) is less than 25 parts by mass, an adhesion property toward a transparent polymer substrate such as a polycarbonate film becomes lower. When an amount of the component (C) is more than 35 parts by mass, there is disadvantages that refractive index of resulting hard coat layer becomes lower and poor visibility may be obtained.

(D) A Polyfunctional Urethane Acrylate Having Three or More Acrylate Groups and an Ester Structure

The hard coating composition according to the present invention contains (D) a polyfunctional urethane acrylate having three or more acrylate groups and an ester structure. By containing the polyfunctional urethane acrylate (D), the hard coat layer obtained to excellent adhesion toward a polycarbonate substrate. Furthermore, the hard coating layer provides a technical effect that the occurrence of interference fringes is prevented, even in case that the hard coat layer has a refractive index within a range of 1.535 to 1.545. The number of acrylate groups is three or more, preferably 3 to 4. When the number of functional groups is less than 3, due to the molecular weight, the reactivity decreases, and there are disadvantages that adhesion and hardness is lowered. On the other hand, when the number of functional groups is too many, adhesion may be reduced due to curing and contraction.

The Polyfunctional acrylate (D) may be obtained by reacting, polycarbonate diol (a) (hereinafter, it may be referred to as a component (a)), a (meth) acrylate compound having two hydroxyl groups and two ethylenically unsaturated groups in the molecule (b) (hereinafter, it may be referred to as a component (b)), with polyisocyanate (c) (hereinafter, it may be referred to as a component (c)).

The polycarbonate diol (a) includes a diol having a straight-chain and branched-chain having 2 to 10 carbon atoms which is represented by HO—(R—O—C(═O)—O)—R′OH, wherein, R and R′ are a same or different alkylene groups having a straight chain or branched chain with 2 to 10 carbon atoms, and the carbon number is the number of the sum of R and R′. Specifically, R and R′ in the above chemical formula includes such as ethylene group, propylene group, butylene group, pentylene group, hexylene group, heptylene group, octylene group, cyclohexylene group, neopentyene group, nonylene group, 2-methyl-1,8-octylene group, or it may be used in combination of two or more thereof. Among these, polycarbonate diols synthesized from 1,5-pentanediol and/or 1,6-hexanediol are preferred. The component (a) may be used one kind of compound or in combination of two or more components (a). In the present invention, ester structure in the polyfunctional acrylate (D) means carbonic acid ester structure derived from a carbonate group of the component (a).

A (meth)acrylate compound (b) containing two hydroxyl groups and two ethylenically unsaturated groups in a molecule may include, specifically, (meth)acrylic acid additive of propylene glycol diglycidyl ether, (meth)acrylic acid additive of 1,6-hexanediol diglycidyl ether, (meth)acrylic acid additive of ethylene glycol diglycidyl ether, (meth)acrylic acid additive of 1,4-butanediol diglycidyl ether, (meth)acrylic acid additive of 1,5-pentanediol diglycidyl ether, (meth)acrylic acid additive of 1,7-heptanediol diglycidyl ether, (meth)acrylic acid additive of 1,8-octanediol diglycidyl ether. In addition, the (meth)acrylate compound (b) may include such as (meth)acrylic acid additive of neopentyl glycol diglycidyl ether, (meth)acrylic acid additive of bisphenol A diglycidyl ether, (meth)acrylic acid additive of hydrogenated bisphenol A diglycidyl ether. Among them, acrylic acid additive of propylene glycol diglycidyl ether, and acrylic acid additive of 1,6-hexanediol diglycidyl ether are preferable.

While a polyisocyanate (c) is not particularly limited, for example, diisocyanate compounds such as an aliphatic diisocyanate compound, an alicyclic diisocyanate compound, an aromatic diisocyanate compound are preferably used. Specifically, the polyisocyanate (c) includes such as tolylene diisocyanate, 4,4′-diphenylmethane diisocyanate, xylylene diisocyanate, xylene diisocyanate, hexamethylene diisocyanate, lysine diisocyanate, 4,4′-methylenebis (cyclohexyl isocyanate), methylcyclohexane-2,4 (or 2,6)-diisocyanate, 1,3-(isocyanatomethyl) cyclohexane, isophorone diisocyanate, trimethylhexamethylene diisocyanate, dimer acid diisocyanate, dianisidine diisocyanate, phenyl diisocyanate, halogenated phenyl diisocyanate, methylene diisocyanate, ethylene diisocyanate, butylene diisocyanate, propylene diisocyanate, octadecylene diisocyanate, 1,5-naphthalene diisocyanate, polymethylene polyphenylene diisocyanate, triphenylmethane triisocyanate, naphthalene diisocyanate, a polymer of tolylene diisocyanate, a polymer of diphenylmethane diisocyanate, a polymer of hexamethylene diisocyanate, 3-phenyl-2-ethylene diisocyanate, cumene-2,4-diisocyanate, 4-methoxy-1,3-phenylene diisocyanate, 4-ethoxy-1,3-phenylene diisocyanate, 2,4′-diisocyanate diphenyl ether, 5,6-dimethyl-1,3-phenylene diisocyanate, 4,4′-diisocyanate diphenyl ether, benzidine diisocyanate, 9,10-anthracene diisocyanate, 4,4′-diisocyanate benzyl, 3,3′-dimethyl-4,4′-diisocyanatodiphenylmethane, 2,6-dimethyl-4,4′-diisocyanate diphenyl, 3,3′-dimethoxy-4,4′-diisocyanate diphenyl, 1,4-anthracene diisocyanate, phenylene diisocyanate, 2,4,6-torirentoriisocyanate, 2,4,4′-triisocyanate diphenyl ether, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 1,10-decamethylene diisocyanate, 1,3 cyclohexylene diisocyanate, 4,4′-methylene-bis(cyclohexyl isocyanate).

Process for the preparation of the polyfunctional urethane acrylate (D) is not particularly limited, for example, the aforementioned (a) to (c) component are added to an organic solvent (e.g., methyl ethyl ketone), and it can be prepared by reacting under the warm conditions if necessary. The termination of the reaction is confirmed when the presence of the isocyanate groups can no longer be confirmed by infrared absorption spectrum. The obtained polyfunctional urethane acrylate (D) may be used with alone or a combination of two or more.

A polyfunctional urethane acrylate (D) preferably has a weight average molecular weight of 20,000 to 60,000, and more preferably have a weight average molecular weight of 30,000 to 50,000. When the weight average molecular weight of the polyfunctional urethane acrylate (D) is too high, viscosity becomes high, smoothness is impaired and interference fringe is deteriorated. When the weight average molecular weight is too low, viscosity becomes low, the smoothness of the coating surface is not maintained and interference fringe is deteriorated.

With regard to an adhesive property, a Polyfunctional urethane acrylate (D) preferably has a hydroxyl value of 0 to 20 mg KOH/g, more preferably of 0 to 5 mg KOH/g. By controlling low hydroxyl value, an adhesive property is maintained after moisture-heat test.

In the present invention, the hard coating composition contains 15 to 25 parts by mass of the component (D) providing that 100 parts by mass of a resin content in the hard coating composition. When an amount of the component (D) is less than 15 parts by mass, adhesion property becomes lower. When an amount of the component (D) is more than 25 parts by mass, the hardness of the hard coat layer becomes low.

Polymerization Initiator and the Like

The hard coating composition according to the present invention may preferably contain a polymerization initiator. Containing a polymerization initiator may provide an excellent polymerization of resin components with an exposure to active energy rays such as ultraviolet rays. The polymerization initiator includes, for example, alkyl phenon type photopolymerization initiator, acyl phosphine oxide type photopolymerization initiator, titanocene type photopolymerization initiator, oxime ester type photopolymerization initiator, and the like. An alkyl phenon type photopolymerization initiator includes, for example, 2,2-dimethoxy-1,2-diphenylethane-1-one, 1-hydroxy cyclohexyl phenyl ketone, 2-hydroxy-2-methyl-1-phenyl propane-1-one, 1-[4-(2-hydroxyethoxy)-phenyl]-2-hydroxy-2-methyl-1-propane-1-one, 2-hydroxy-1-{4-[4-(2-hydroxy-2-methyl propionyl) benzyl] phenyl}-2-methyl propan-1-one, 2-methyl-1-(4-methylthiophenyl)-2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1, 2-(dimethylamino)-2-[(4-methylphenyl)methyl]-1-[4-(4-morpholinyl)phenyl]-1-butanone and the like. An acyl phosphine oxide type photopolymerization initiator includes, for example, 2,4,6-trimethyl benzoyl diphenyl phosphine oxide, bis(2,4,6-trimethyl benzoyl) phenyl phosphine oxide and the like. A titanocene type photopolymerization initiator includes, for example, bis(η5-2,4-cyclopentadiene-1-yl)-bis(2,6-difluoro-3-(1H-pyrrol-1-yl)phenyl)titanium and the like. An oxime ester type photopolymerization initiator includes, for example, 1.2-octanedione, 1-[4-(phenylthio)-, 2-(O-benzoyloxime)], ethanone, 1-[9-ethyl-6-(2-methyl benzoyl)-9H-carbazole-3-yl]-, 1-(0-acetyl oxime), oxyphenylacetic acid, 2-[2-oxo-2-phenyl acetoxy ethoxy] ethyl ester, 2-(2-hydroxy ethoxy) ethyl ester and the like. These photopolymerization initiator may be used with alone or a combination of two or more.

In the above photopolymerization initiators, 2-hydroxy-2-methyl-1-phenyl propan-1-one, 1-hydroxy cyclohexyl phenyl ketone, 2-methyl-1-(4-methylthiophenyl)-2-morpholinopropan-1-one, 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl) butanone-1, and 2,2-dimethoxy-1,2-diphenyl ethan-1-one and the like may be preferably used.

A preferable amount of the photopolymerization initiator may be 0.01 to 20 parts by mass, more preferably 1 to 10 parts by mass, providing that 100 parts by mass of the components (A), (B), (C) and (D) (a total of all these components is called “resin components”).

The hard coating composition used in the present invention may contain a solvent. A solvent is not limited and may be appropriately selected with consideration of the components of the hard coating composition, a type of a substrate to be applied, means for application and the like. A solvent includes, for example, aromatic solvents such as toluene, xylene; ketone solvents such as methyl ethyl ketone, acetone, methyl isobutyl ketone, cyclohexanone; ether solvents such as diethyl ether, isopropyl ether, tetrahydrofuran, dioxane, ethyleneglycol dimethyl ether, ethyleneglycol diethyl ether, diethyleneglycol dimethyl ether, diethyleneglycol diethyl ether, propyleneglycol monomethyl ether, anisole, phenetole; ester solvents such as ethyl acetate, butyl acetate, acetic acid isopropyl, ethylene glycol diacetate; amide solvents such as dimethylformamide, diethylformamide, N-methylpyrrolidon; cellosolve solvents such as methylcellosolve, ethylcellosolve, butyl cellosolve; alcohol solvents such as methanol, ethanol, propanol; halogen solvents such as dichloromethane, chloroform; and the like. The solvent may be used with alone or a combination of two or more. In the above solvents, ester solvents, ether solvents, alcohol solvent and ketone solvent may preferably be used.

The hard coating composition may optionally contain an additive. The additive includes conventional additives such as an antistatic agent, a plasticizer, a surfactant, an antioxidant and the like.

The hard coating composition has a technical feature that the hard coating composition can provide a hard coat layer with an high refractive index even if the hard coating composition does not contain a high refractive index material of metal oxide such as ZnO, TiO₂, CeO₂, SnO₂, ZrO₂ and indium tin oxide. Therefore, the hard coating composition may preferably contain no metal oxide high refractive index materials selected from the group consisting of ZnO, TiO₂, CeO₂, SnO₂, ZrO₂ and indium tin oxide. For more details, a total content of ZnO, TiO₂, CeO₂, SnO₂, ZrO₂ and indium tin oxide in the hard coating composition may preferably be less than or equal to 0.0001% by mass. When the high refractive index materials such as a metal oxide are included in a hard coat layer, the hard coat layer generally has inferior stretchability and bending resistance compared with a hard coat layer without the high refractive index materials.

The hard coat layer formed by applying the hard coating composition preferably has excellent hardness as a hard coat layer and has a high refractive index within a range of 1.535 to 1.545. When the hard coat layer has a refractive index in this range, there is an advantage that it is possible to favorably suppress occurrence of interference fringes in the transparent electroconductive laminate.

The hard coat layer obtained by applying the hard coating composition has a technical characteristic of having excellent stretchability and adhesion property toward a polycarbonate substrate, as well as excellent visibility and excellent hardness which is required in the field of a hard coat layer. The excellent stretchability can provide remarkably-improved visibility of the transparent electroconductive laminate and is advantageous. According to a process for manufacturing a transparent electroconductive laminate, in a process for applying a transparent electrically conducting layer, a substrate film having a hard coat layer tends to be exposed to a partial load. For example, the partial load may cause a swell or a kink of a film which results from a difference of thermal shrinkage and/or thermal expansion among a hard coat layer and a substrate film. The swell or the kink of a film provides deterioration of visibility due to visually distinguish about presence or absence of a transparent electrically conductive layer such as ITO. The deterioration of visibility distinctly deteriorates visibility of a touch panel.

The hard coat layer obtained by applying the hard coating composition has a technical characteristic of having stretchability, as well as excellent visibility and excellent hardness which is required in the field of a hard coat layer. Since the hard coat layer of the present invention has excellent extensibility, even if the substrate film is locally thermally expanded by heating in the step of applying a transparent electrically conductive layer, the hard coat layer can have an excellent followability. Therefore, it is advantageous that deterioration of visibility due to visually distinguish about presence or absence of a transparent electrically conductive layer such as ITO is solved. In addition, the electroconductive laminate of the present invention has high adhesion to a polycarbonate substrate, thus, it can be maintained in excellent condition in a higher level of an adhesion test (severe adhesion test). Furthermore, the electroconductive laminate is free of the resin component that may volatilize during heat treatment of the electroconductive laminate carried out at 130° C. for 2 hours. Therefore, there is an advantage that a defect does not occur to inhibit the crystallization of the upper electrically conductive layer.

The hard coat layer is formed applying the hard coating composition on a polycarbonate substrate. A method for applying the hard coating composition can be accordingly selected depending on conditions of the hard coating composition and a coating process, and may include, for example, a dip coating method, an air knife coating method, a curtain coating method, a roller coating method, a wire bar coating method, a gravure coating method, an extrusion coating method (in U.S. Pat. No. 2,681,294) and the like.

A thickness of the hard coat layer is not limited and can be accordingly selected depending on various conditions. For example, the hard coating composition may be applied so as to obtain a hard coating layer having a thickness of 0.01 μm to 20 μm.

A hard coat layer is formed by curing a coating film obtained by applying of the hard coating composition. The curing may be caused by irradiation of light, by a light source which emits active energy ray with suitable wavelength. As the irradiation of active energy ray, a light having exposure value of, for example, 0.1 to 1.5 J/cm², preferably 0.3 to 1.5 J/cm², may be used. A wavelength region of the irradiation of light is not limited and may appropriately be, for example, not greater than 360 nm. A light with such wavelength can be obtained by a high-pressure mercury lamp, an extra high-pressure mercury lamp and the like.

The hard coat layer of the present invention preferably has a glass transition temperature of 60 to 80° C. When the glass transition temperature is within the above range, there is an advantage that it exhibits high extensibility in the step of manufacturing the touch panel electrodes, and the pattern of the transparent electrically conductive layer becomes difficult to see. When the glass transition temperature is less than 60° C., no sufficient hardness is obtained in a hard coat film, and there is a possibility that whitening occurs during the film forming of the transparent electrically conductive layer. On the other hand, when the glass transition temperature of the hard coat layer is higher than 80° C., extensibility is impaired, and it may become impossible to obtain a technical effect of obscuring the pattern of the transparent electrically conductive layer.

Color Difference Adjusting Layer

The electroconductive laminate according to the present invention has a color difference adjusting layer on a hard coat layer. The color difference adjusting layer may preferably be a layer existing between the hard coat layer and a transparent electrically conducting layer. The color difference adjusting layer may be a single layer or may be a layer composed of two or more layers. The color difference adjusting layer is a layer for improving the adhesion between layers and the optical properties (the transmittance, the color tone and the like) of the transparent electroconductive laminate.

In the present invention, the color difference adjusting layer is a layer containing a curing resin component (i), and metal oxide particles having an average primary particle diameter of 100 nm or less (ii) and/or metal fluoride particles having an average primary particle diameter of 100 nm or less (iii). In this context, provided that the total mass of the particles (ii) and (iii) in the color difference adjusting layer lies within the range of 0 to 200 parts by mass with respect to 100 parts by mass of the curing resin component (i).

As the curing resin component (i), an ultraviolet curing resin or a thermosetting resin can be used. With regard to the color difference adjusting layer in the present invention, it is more preferred that an ultraviolet curing resin be used as the curing resin component (i).

The ultraviolet curing resin can be obtained from a composition containing a monomer having ultraviolet curing performance. Examples of the monomer having ultraviolet curing performance include monofunctional and polyfunctional acrylates such as a polyol acrylate, a polyester acrylate, a urethane acrylate, an epoxy acrylate, a modified styrene acrylate, a melamine acrylate and a silicon-containing acrylate.

Specific examples of the monomer include trimethylolpropane trimethacrylate, a trimethylolpropane ethylene oxide-modified acrylate, a trimethylolpropane propylene oxide-modified acrylate, an isocyanuric acid alkylene oxide-modified acrylate, pentaerythritol triacrylate, dipentaerythritol hexaacrylate, dimethylol tricyclodecane diacrylate, tripropylene glycol triacrylate, diethylene glycol diacrylate, 1,6-hexanediol diacrylate, an epoxy-modified acrylate, a urethane-modified acrylate such as a urethane (meth)acrylate, and a polyfunctional monomer such as an epoxy-modified acrylate. These monomers may be used alone or two or more thereof may be used together.

Of these monomers having ultraviolet curing performance, a urethane-modified acrylate is preferred. As the urethane-modified acrylate, a commercial product thereof can be used, and for example, products in the SHIKOH series available from The Nippon Synthetic Chemical Industry Co., Ltd. such as UV1700B, UV6300B, UV765B, UV7640B and UV7600B; products in the Art Resin series available from Negami Chemical Industrial Co., Ltd. such as Art Resin HDP, Art Resin UN9000H, Art Resin UN3320HA, Art Resin UN3320HB, Art Resin UN3320HC, Art Resin UN3320HS, Art Resin UN901M, Art Resin UN902MS and Art Resin UN903; UA100H, U4H, U6H, U15HA, UA32P, U6LPA, U324A, U9HAMI and the like available from Shin Nakamura Chemical Co., Ltd.; products in the Ebecryl series available from Daicel-UCB Co. Ltd., such as 1290, 5129, 254, 264, 265, 1259, 1264, 4866, 9260, 8210, 204, 205, 6602, 220 and 4450; products in the BEAMSET series available from ARAKAWA CHEMICAL INDUSTRIES, LTD., such as 371, 371MLV, 371S, 577, 577BV and 577AK; products in the RQ series available from MITSUBISHI RAYON CO., LTD.; products in the UNIDIC series available from DIC Corporation; DPHA40H (available from Nippon Kayaku Co., Ltd.), CN9006 and CN968 (available from SARTOMER company), and the like can be used.

In the case where the curing resin component (i) is an ultraviolet curing resin, it is preferred that a composition forming the color difference adjusting layer contain a photopolymerization initiator. As the photopolymerization initiator, for example, a photopolymerization initiator commonly used such as acetophenone, benzophenone, benzoin, benzoylbenzoate and thioxanthone can be used.

The composition forming the color difference adjusting layer may further contain a photosensitizer. As the photosensitizer, for example, a photosensitizer commonly used such as triethylamine and tri-n-butylphosphine can be used.

The composition forming the color difference adjusting layer may further contain hydrolysates of various alkoxysilanes.

In the case where the curing resin component (i) is a thermosetting resin, the composition forming the color difference adjusting layer may contain a thermosetting monomer such as an organosilane-based thermosetting monomer in which a silane compound such as methyltriethoxysilane or phenyltriethoxysilane constitutes a monomer, a melamine-based thermosetting monomer in which an etherified methylolmelamine or the like constitutes a monomer, an isocyanate-based thermosetting monomer, a phenol-based thermosetting monomer and an epoxy-based thermosetting monomer. These thermosetting monomers may be used alone or two or more thereof may be used in combination. In addition to the above-mentioned thermosetting monomer, the composition may contain a thermoplastic resin component as necessary.

In the case where the curing resin component (i) is a thermosetting resin, it is preferred that the composition forming the color difference adjusting layer contains a reaction accelerator or a curing agent. Examples of the reaction accelerator include triethylenediamine, dibutyltin dilaurate, benzyl methylamine, pyridine and the like. Examples of the curing agent include methylhexahydrophthalic anhydride, 4,4′-diaminodiphenylmethane, 4,4′-diamino-3,3′-diethyldiphenylmethane, diaminodiphenylsulfone and the like.

In the present invention, in addition to the above-mentioned curing resin component (i), metal oxide particles having an average primary particle diameter of 100 nm or less (ii) and/or metal fluoride particles having an average primary particle diameter of 100 nm or less (iii) are contained in the color difference adjusting layer. Then, provided that the total mass of these particles (ii) and (iii) lies within the range of 0 to 200 parts by mass with respect to 100 parts by mass of the curing resin component (i). The total mass of the particles (ii) and (iii) can be appropriately adjusted depending on the refractive index of each of (i), (ii) and (iii) in order to attain desired optical properties. From the viewpoint of film strength after curing, it is preferred that the total mass lie within the range of 1 to 150 parts by mass, and it is more preferred that the total mass lie within the range of 1 to 100 parts by mass, with respect to 100 parts by mass of the curing resin component (i).

In the case where the total mass of the particles (ii) and (iii) in the color difference adjusting layer exceeds 200 parts by mass, there occurs a defect that the adhesion between layers is deteriorated.

Specific examples of the metal oxide particles (ii) include ZnO, TiO₂, CeO₂, SnO₂, ZrO₂, an indium-tin oxide and the like. Any of these metal oxide particles (ii) are characterized as having a high refractive index. On that account, a color difference adjusting layer in which the metal oxide particles (ii) are contained basically becomes a high refractive index layer. As the metal oxide particle (ii), ZnO, TiO₂ and ZrO₂ are more preferably used. The metal oxide particles (ii) may be used alone or two or more thereof may be used together.

In this connection, as described above, provided that any of these metal oxide particles (ii) have an average primary particle diameter of 100 nm or less. In the case where the average primary particle diameter exceeds 100 nm, there occurs a defect that the haze value rises, drawbacks in appearance such as the formation of a lump like foreign materials are caused since the particles of a visible size are easily formed due to aggregation of particles and the like at the time of forming the color difference adjusting layer. In the present specification, the average primary particle diameter refers to a 50% volume particle diameter at the time of measuring a liquid prepared by dispersing particles in a solvent such as n-butyl alcohol with a particle size analyzer.

Specific examples of a metal constituting the metal fluoride particles (iii) include calcium, barium, magnesium, strontium and the like. Of these metals, it is more preferred that the metal be magnesium. These metal fluoride particles (iii) may be used alone or two or more thereof may be used together. In this connection, as necessary, the metal fluoride particles (iii) and SiO₂ may be used in combination.

Any of these metal fluoride particles (iii) are characterized as having a low refractive index. On that account, a color difference adjusting layer in which the metal fluoride particles (iii) are contained basically becomes a low refractive index layer. In this connection, as described above, provided that any of these metal fluoride particles (iii) have an average primary particle diameter of 100 nm or less. In the case where the average primary particle diameter exceeds 100 nm, there occurs a defect that the haze value rises, drawbacks in appearance such as the formation of a lump like foreign materials are caused, since the particles of a visible size are easily formed due to aggregation of particles and the like at the time of forming the color difference adjusting layer.

The color difference adjusting layer in the present invention may be composed of a single layer or may be composed of two or more layers. In the case where the color difference adjusting layer is a single layer, it is preferred that the layer be a high refractive index layer containing the metal oxide particles (ii). Examples of another aspect thereof include an aspect containing both the metal oxide particles (ii) and the metal fluoride particles (iii) mentioned above. The thickness of the color difference adjusting layer in the case where the color difference adjusting layer is a single layer is preferably 30 to 300 nm, more preferably 50 nm to 200 nm.

Moreover, for example, in the case where the color difference adjusting layer is a layer composed of two layers, it is preferred that the layer have a two-layered structure composed of a high refractive index layer containing the metal oxide particles (ii) and a low refractive index layer containing the metal fluoride particles (iii). In this case, it is more preferred to be an aspect in which a hard coat layer and the high refractive index layer are brought into contact with each other. In the case where the color difference adjusting layer is constituted of two layers composed of one layer of a high refractive index layer and one layer of a low refractive index layer, the thickness of the whole color difference adjusting layer is preferably 30 to 300 nm, more preferably 50 nm to 200 nm.

With regard to the formation of the color difference adjusting layer, for example, the layer can be formed by applying a composition containing a monomer having ultraviolet curing performance and the metal oxide particles (ii) and/or the metal fluoride particles (iii) on a hard coat layer of a transparent polymer substrate having the hard coat layer, and then, irradiating the composition with active energy rays such as ultraviolet rays to cure the composition. Alternatively, the layer can be formed by applying a composition containing a thermosetting monomer and the metal oxide particles (ii) and/or the metal fluoride particles (iii) on a hard coat layer of a transparent polymer substrate having the hard coat layer, and then; thermally curing the composition.

As an example of the case where the color difference adjusting layer is a layer composed of two layers, a color difference adjusting layer composed of two layers can be formed by firstly applying a composition containing the metal oxide particles (ii) on a hard coat layer and curing the composition, and then, applying a composition containing the metal fluoride particles (iii) and curing the composition.

As another example of the case where the color difference adjusting layer is a layer composed of two layers, a color difference adjusting layer composed of two layers can be formed by firstly applying a composition containing the metal fluoride particles (iii) on a hard coat layer and curing the composition, and then, applying a composition containing the metal oxide particles (ii) and curing the composition.

Examples of a method for applying the composition include an applying method using a coating machine such as a doctor knife, a bar coater, a gravure roll coater, a curtain coater, a knife coater or a spin coater which is usually performed by a person skilled in the art, an applying method using a spray, an applying method by immersion and the like.

Moreover, the composition may contain an organic solvent as necessary. Examples of the organic solvent include alcohol-based solvents such as ethanol, isopropyl alcohol, butanol and 1-methoxy-2-propanol, hydrocarbon-based solvents such as hexane, cyclohexane, ligroin and cyclohexanone, ketone-based solvents such as methyl isobutyl ketone and isobutyl acetate, aromatic hydrocarbon-based solvents such as xylene and toluene, and the like. These organic solvents may be used alone or two or more thereof may be used together.

In the case of curing a composition containing a monomer having ultraviolet curing performance, the curing can be performed by using a light source emitting active energy rays of a required wavelength and irradiating the composition with the active energy rays. As the active energy ray to be irradiated, for example, light of 0.1 to 1.5 J/cm² in terms of an exposure quantity, preferably light of 0.3 to 1.5 J/cm², can be used. Moreover, although the wavelength of the irradiation light is not particularly limited, for example, irradiation light having a wavelength of 360 nm or less and the like can be used. Such light can be obtained by using a high pressure mercury lamp, an ultra-high pressure mercury lamp or the like.

Moreover, in the case of curing a composition containing a thermosetting monomer, for example, the composition can be cured by heating at 60 to 140° C. for 1 to 60 minutes. In this context, the heating temperature and the heating time can be selected according to the kind of the thermosetting monomer contained in the composition.

Electrically Conducting Layer and Electroconductive Laminate

With regard to the electroconductive laminate according to the present invention, an electrically conducting layer is generally formed on the hard coat layer or the color difference adjusting layer. The electrically conducting layer may be a transparent electrically conducting layer where whole of an electroconductive laminate is transparent, and may be a metal electrically conducting layer where an electroconductive laminate is not transparent. Although no particular restriction is put on the constituent material for the transparent electrically conducting layer, examples thereof include a metal layer and a metal compound layer. Examples of a component constituting the transparent electrically conducting layer include a layer of a metal oxide such as silicon oxide, aluminum oxide, titanium oxide, magnesium oxide, zinc oxide, indium oxide and tin oxide. Of these, a crystalline layer composed mainly of indium oxide is preferred, and in particular, a layer composed of crystalline ITO (Indium Tin Oxide) is preferably used.

Moreover, in the case where the transparent electrically conducting layer is composed of crystalline ITO, although it is not particularly necessary to provide an upper limit to the crystal grain size, it is preferred that the crystal grain size be 500 nm or less. When the crystal grain size exceeds 500 nm, it is not preferred because the bending durability deteriorates. In this context, the crystal grain size is defined as a maximum size among diagonal lines or diameters in each area having a polygonal shape or an elliptical shape observed with a transmission electron microscope (TEM). In the case where the transparent electrically conducting layer is composed of amorphous ITO, the environmental reliability may be lowered.

The electrically conducting layer can be formed by a known method, and for example, a physical vapor deposition method such as a DC magnetron sputtering method, an RF magnetron sputtering method, an ion plating method, a vacuum vapor deposition method or a pulse laser deposition method can be used. In the case where attention is paid to industrial productivity such that a metal compound layer with a uniform film thickness is formed on a large area, a DC magnetron sputtering method is desirable. In this connection, although a chemical vapor deposition method such as a chemical vapor phase deposition method or a sol-gel method can also be used in addition to the physical vapor deposition method (PVD method), from the viewpoint of film thickness control, a sputtering method is still desirable.

The film thickness of the electrically conducting layer is preferably 5 to 50 nm from the points of transparency and electrical conductivity. The film thickness is further preferably 5 to 30 nm. When the film thickness of the electrically conducting layer is less than 5 nm, there is a tendency that stability resistance value with the lapse of time lowers. When the film thickness exceeds 50 nm, an electroconductive laminate prepared with the electrically conducting layer is not preferred as a touch panel because of lowering in bending durability.

In the case where the electroconductive laminate according to the present invention is used as a touch panel, from aspects of reduction in power consumption of a touch panel, the need for circuit processing and the like, it is preferred that a transparent electrically conducting layer in which the surface resistance value of the transparent electrically conducting layer with a film thickness of 10 to 40 nm lies within the range of 10 to 2000 Ω/square, more preferably 30 to 1000 Ω/square, be used.

In this connection, as the transparent electrically conducting layer, a layer formed by coating a dispersion prepared by dispersing a metal nanowire, a carbon nanotube, electroconductive oxide fine particles and the like on a polymer substrate by a wet process (for example, a spin coating method, gravure coating, slot die coating, or printing) can also be used.

The electrically conducting layer thus formed is subjected to pattern formation by an etching treatment. The etching treatment is generally performed by covering the electrically conducting layer with a mask for forming a pattern, and then, etching the electrically conducting layer with an etchant such as an acid aqueous solution. Examples of the etchant include inorganic acids such as hydrogen chloride, hydrogen bromide, sulfuric acid, nitric acid and phosphoric acid, organic acids such as acetic acid, a mixture thereof, and an aqueous solution thereof. Specific examples of the etchant include a strong acid aqueous solution obtained by a mixing of 12 N hydrochloric acid, 16 N nitric acid and water in a mass ratio of 12 N hydrochloric acid:16 N nitric acid:water being 3.3:1.0:7.6.

In this connection, a heat treatment may be performed as necessary before or after patterning the electrically conducting layer. In the case where the electrically conducting layer is composed of ITO which crystallizes by the heat treatment, by performing a heat treatment, there is an advantage that the transparency and the electrical conductivity can be enhanced. For example, the heat treatment can be performed by heating at 100 to 150° C. for 15 to 180 minutes.

The electroconductive laminate according to the present invention is characterized as having a difference ΔR of R1 and R2 of not greater than 1, wherein R1 is a reflectance obtained by irradiation with a light source having a wavelength in a range of 500 to 750 nm toward the electroconductive laminate, and R2 is a reflectance obtained by irradiation with a light source having a wavelength in a range of 500 to 750 nm toward a electroconductive laminate after immersion into a strong acid aqueous solution at 40° C. for three minutes and dried, wherein the strong acid aqueous solution is obtained by a mixing of 12 N hydrochloric acid, 16 N nitric acid and water in a mass ratio of 12 N hydrochloric acid:16 N nitric acid:water being 3.3:1.0:7.6.

The strong acid aqueous solution is a strong acid aqueous solution which is so-called aqua regia commonly used in an etching treatment. By performing an etching treatment with the strong acid aqueous solution, it follows that the electrically conducting layer is etched. FIG. 1 is a schematic explanatory view showing an electroconductive laminate subjected to an etching treatment. An electroconductive laminate (10) has a structure in which a hard coat layer (3), a color difference adjusting layer (5), and a transparent electrically conducting layer (7) are formed in this order on one surface of a polycarbonate substrate (1). In this context, the portion shown by a reference numeral (11) is a portion from which the transparent electrically conducting layer (7) was eliminated by patterning by an etching treatment, and the portion shown by a reference numeral (13) is a portion which had been covered with a mask at the time of the etching treatment and a portion in which the electrically conducting layer has been left as it is. In this context, the reflectance R1 means a reflectance at the portion of the reference numeral (13) in FIG. 1, and the reflectance R2 means a reflectance at the portion of the reference numeral (11) in FIG. 1. Then, the electroconductive laminate according to the present invention is characterized as having a difference ΔR of R1 and R2 of not greater than 1, which are reflectances obtained by irradiation with a light source having a wavelength in a range of 500 to 750 nm. That is, in the electroconductive laminate according to the present invention, there is almost no difference of reflectance between a part where the electrically conducting layer (7) exists and a part where the electrically conducting layer (7) does not exist. This achieves an extremely high level of visibility.

With regard to the measurement of the reflectance of the electroconductive laminate, for example, using a spectrophotometer such as U-3000 available from Hitachi, Ltd., the spectral reflectance at an incident angle of 10° can be measured in accordance with JIS K5600-4-5.

Antiblocking Layer

The electroconductive laminate according to the present invention has a structure in which a hard coat layer, a color difference adjusting layer, and an electrically conducting layer are formed in this order on one surface of a polycarbonate substrate. The electroconductive laminate may optionally have an antiblocking layer formed on the other side of the polycarbonate substrate. Forming the antiblocking layer on the other side of the substrate can prevent occurrence of blocking in a production process of the electroconductive laminate, which provides improved preservation stability.

A composition for forming an antiblocking layer includes, for example, a composition for an antiblocking layer containing a first component and a second component. It may be preferable that the composition is a composition for an antiblocking layer in which a difference of SP values (ΔSP) of the first component (SP1) and the second component (SP2) is within a range of 1 to 2, and phase separation occurs between the first component and the second component after the composition for forming an antiblocking layer is applied, to form an antiblocking layer having a microscopic convexoconcave on its surface.

An unsaturated double bond containing acrylic copolymer is used as the first component. The unsaturated double bond containing acrylic copolymer includes, for example,

a resin obtained by copolymerization of (meth)acrylic monomer and other ethylenically unsaturated double bond containing monomer;

a resin obtained by a reaction of (meth)acrylic monomer with other ethylenically unsaturated double bond and epoxy group containing monomer; and

a resin obtained by addition reaction of a component having both of an unsaturated double bond and other functional group, for example, acrylic acid or glycidyl acrylate, to a resin obtained by a reaction of (meth)acrylic monomer with other ethylenically unsaturated double bond and isocyanate containing monomer. These unsaturated double bond containing acrylic copolymers can be used with alone or a combination of two or more. The unsaturated double bond containing acrylic copolymer may preferably have a weight-average molecular weight of 2000 to 100000, more preferably 5000 to 50000.

A polyfunctional unsaturated double bond containing monomer or oligomer thereof may be preferably used as the second component (monomer or oligomer). An “oligomer” used in the present specification means a polymerization product having a repeat unit, in which the number of the repeat unit is 3 to 10. The polyfunctional unsaturated double bond containing monomer includes, for example, a polyfunctional acrylate obtained by dealcoholization reaction of a polyalcohol and (meth)acrylate, specifically, dipentaerythritol hexa(meta)acrylate, dipentaerythritol penta(meta)acrylate, trimethylol propane tri(meta)acrylate, ditrimethylolpropane tetra(meta)acrylate, neopentylglycol di(meta)acrylate, and the like. In addition, an acrylate monomer having polyethylene glycol structure such as polyethylene glycol #200 diacrylate (produced by Kyoeisha Chemical Co., Ltd.) may be used. These polyfunctional unsaturated double bond containing monomers can be used with alone or a combination of two or more. The second component may preferably be a polyfunctional acrylate.

In case that the first component and the second component are the above combinations, a suitable solvent includes, for example, a ketone solvent such as methyl ethyl ketone, acetone, methyl isobutyl ketone, cyclohexanone and the like; an alcohol solvent such as methanol, ethanol, propanol, isopropanol, butanol and the like; an ether solvent such as anisole, phenetole, propylene glycol monomethylether, ethyleneglycol dimethyl ether, ethyleneglycol diethyl ether, diethyleneglycol dimethyl ether, diethyleneglycol diethyl ether, and the like. These solvents may be used with alone or a combination of two or more.

The composition for forming an antiblocking layer may preferably contain a photopolymerization initiator. The photopolymerization initiator includes, for example, 2-hydroxy-2-methyl-1-phenyl propan-1-one, 1-hydroxy cyclohexyl phenyl ketone, 2-methyl-1-[4-(methylthio)phenyl]-2-morpholino propan-1-one, 2,2-dimethoxy-1,2-diphenylethan-1-one, 2-benzyl-2-dimethylamino-1-(4-morpholino phenyl)-butanone-1, and the like.

In the composition for forming an antiblocking layer, a difference of SP values of the first component and the second component provides phase separation. An antiblocking layer having microscopic convexoconcave on its surface can be formed by the phase separation. The difference of SP values of the first component and the second component may preferably be not less than 1, more preferably within a range of 1 to 2.

When the difference of the first component and the second component is not less than 1, the first component and the second component are less compatible. Thus phase separation seems to occur between the first component and the second component after the composition for forming an antiblocking layer is applied.

A SP value means a solubility parameter, and is a criterion for solubility. The more SP value means a higher polarity, and the little SP value means a lower polarity.

The SP value can be determined by the following procedure.

-   Reference: Suh, Clarke [J.P.S.A.-1, 5, 1671-1681 (1967)]     Measuring temperature: 20° C.     Sample: A resin (0.5 g) is measured and is put into a 100 ml beaker,     next, 10 ml of a good solvent is added using a whole pipette and is     dissolved by means of a magnetic stirrer.     Solvent:     Good solvent: Dioxane, acetone, and the like     Poor solvent: n-Hexane, deionized water, and the like     Determination of cloud point: Using a 50 ml biuret, the poor solvent     is dropped and read the amount dripped up to the point where     clouding takes place.

A SP value δ of a resin is given by the following equation: δ=(V _(ml) ^(1/2)δ_(ml) +V _(mh) ^(1/2)δ_(mh))/(V _(ml) ^(1/2) +V _(mh) ^(1/2)) V _(m) =V ₁ V ₂/(φ₁ V ₂+φ₂ V ₁) δ_(m)=φ₁δ₁+φ₂δ₂ V_(i): a molar volume of each solvent (ml/mol) φ_(i): a volume fraction of each solvent at cloud point δ_(i): a SP value of each solvent ml: low SP poor solvent mixture system mh: high SP poor solvent mixture system

The composition for forming an antiblocking layer may further contain conventional additives such as an antistatic agent, a plasticizer, a surfactant, an antioxidant, an ultraviolet absorber and the like.

The composition for forming an antiblocking layer may contain a conventional resin component in addition to the first component and the second component. The composition for forming an antiblocking layer has a technical feature of obtaining a resin layer with convexoconcave without including particles such as resin particles. Therefore the composition for forming an antiblocking layer may preferably include no resin particles. On the other hand, the composition for forming an antiblocking layer may optionally contain at least one of inorganic particles, organic particles and a complex material thereof. These particles can be added not for the purpose of forming convexoconcave on a surface of the resin layer. These particles can be added for the purpose of controlling phase separation and a segregation to obtain more microscopic convexoconcave. These particles may have a mean diameter of not greater than 0.5 μm, preferably 0.01 μm to 0.3 μm. When the mean diameter is more than 0.5 μm, a transparency may slightly be deteriorated.

Examples of the inorganic particles include at least one selected from the group consisting of silica, alumina, titania, zeolite, mica, synthetic mica, calcium oxide, zirconium oxide, zinc oxide, magnesium fluoride, smectite, synthetic smectite, vermiculite, ITO (indium oxide/tin oxide), ATO (antimony oxide/tin oxide), tin oxide, indium oxide and antimony oxide.

Examples of the organic particles include at least one selected from the group consisting of acrylic, olefin, polyether, polyester, urethane, polyester, silicone, polysilane, polyimide and fluorine particles.

The composition for forming an antiblocking layer can be prepared by mixing the first component and the second component, and an optional solvent, and optional additives such as a photopolymerization initiator, a catalyst, a photosensitizer. A mass ratio of the first component and the second component in the composition for forming an antiblocking layer may preferably satisfy the following formula,

the first composition:the second composition being 0.1:99.9 to 50:50, more preferably 0.3:99.7 to 20:80, most preferably 0.5:99.5 to 10:90. In case that an additive such as a photopolymerization initiator, a catalyst or a photosensitizer are included in the composition, total amount of the additives may preferably be 0.01 to 20 parts by mass providing that 100 parts by mass of a total mass of the first component and the second component (a total of all these components is called “resin components”), more preferably 1 to 10 parts by mass. In case that a solvent are included in the composition, an amount of the solvent may preferably be 1 to 9900 parts by mass providing that 100 parts by mass of a total mass of the first component and the second component, more preferably 10 to 900 parts by mass.

The composition for forming an antiblocking layer is applied and cured to form an antiblocking layer having a microscopic convexoconcave on its surface. A method for applying the composition for forming an antiblocking layer may include, for example, a dip coating method, an air knife coating method, a curtain coating method, a roller coating method, a wire bar coating method, a gravure coating method, an extrusion coating method and the like. A thickness of the antiblocking layer may be, for example 0.01 μm to 20 μm.

After applying the composition for forming an antiblocking layer, phase separation and curing are generated by irradiation of light. As the irradiation of light, a light having exposure value of, for example, 0.1 to 3.5 J/cm², preferably 0.5 to 1.5 J/cm², may be used. A wavelength region of the irradiation of light is not limited and may appropriately be, for example, not greater than 360 nm. A light with such wavelength can be obtained by a high-pressure mercury lamp, an extra high-pressure mercury lamp and the like.

Touch Panel

A touch panel according to the present invention has the transparent electroconductive laminate. The touch panel according to the present invention includes, for example, an electrostatic capacity type touch panel. The transparent electroconductive laminate according to the present invention may also be used in a resistive film type touch panel.

An embodiment of layer formation in use of the transparent electroconductive laminate as a substrate for a touch panel includes the following constructions:

a transparent electrically conductive layer/a color difference adjusting layer/a hard coat layer/a polycarbonate substrate;

a transparent electrically conductive layer/a hard coat layer/a polycarbonate substrate;

a transparent electrically conductive layer/a color difference adjusting layer/a hard coat layer/a polycarbonate substrate/an antiblocking layer;

a transparent electrically conductive layer/a hard coat layer/a polycarbonate substrate/an antiblocking layer;

a transparent electrically conductive layer/a color difference adjusting layer/a hard coat layer/a polycarbonate substrate/a hard coat layer/a color difference adjusting layer/a transparent electrically conductive layer;

a transparent electrically conductive layer/a hard coat layer/a polycarbonate substrate/a hard coat layer/a color difference adjusting layer/a transparent electrically conductive layer;

an auxiliary electrode layer/a transparent electrically conductive layer/a color difference adjusting layer/a hard coat layer/a polycarbonate substrate;

an auxiliary electrode layer/a transparent electrically conductive layer/a hard coat layer/a polycarbonate substrate;

an auxiliary electrode layer/a transparent electrically conductive layer/a color difference adjusting layer/a hard coat layer/a polycarbonate substrate/an antiblocking layer;

an auxiliary electrode layer/a transparent electrically conductive layer/a color difference adjusting layer/a hard coat layer/a transparent polymer substrate/an antiblocking layer;

an auxiliary electrode layer/a transparent electrically conductive layer/a color difference adjusting layer/a hard coat layer/a polycarbonate substrate/a hard coat layer/a color difference adjusting layer/a transparent electrically conductive layer/an auxiliary electrode layer;

an auxiliary electrode layer/a transparent electrically conductive layer/a hard coat layer/a polycarbonate substrate/a hard coat layer/a transparent electrically conductive layer/an auxiliary electrode layer.

The above-mentioned layer constitution means an order of from a top layer to a bottom layer. A metal-oxide layer, for example, a layer composed of a metal oxide such as silicon dioxide or niobium oxide, molybdenum oxide, may be formed directly under the a transparent electrically conductive layer in order to improve a color difference adjusting or adhesion property. A hard coat layer for surface protection may be formed on a transparent electrically conductive layer as a top layer. In that case, the hard coat layer may be the hard coat layer according to the present invention, or may be a conventional hard coat layer other than the hard coat layer according to the present invention.

The auxiliary electrode layer referred to herein means a layer usable as an electrode material for wiring. As the material of the auxiliary electrode layer, one with a specific resistance of 1×10⁻⁶ Ωcm or more and 1×10⁻⁴ Ωcm or less is desirable. When a metal material with a specific resistance of less than 1×10⁻⁶ Ωcm is used, the layer is unstable from the viewpoints of uses and functions and it becomes difficult to form the layer as a thin film. On the other hand, when a metal material with a specific resistance of more than 1×10⁻⁴ Ωcm is used, the resistance value becomes higher at the time of forming fine wiring since the resistance value is too high. For the foregoing reasons, as a metal suitable for practical use, a single metal selected from the group of Cu, Ag, Al, Au, Ni, Ni/Cr and Ti, or an alloy composed of a plurality of metals is recommended. In particular, from the points of being a metal which is high in electrical conductivity and excellent in processability such as pattern etching and electroplating, being satisfactory in electrical and mechanical connectability between an electrode and a lead part of a circuit or the like (solder, an anisotropic conductive connector and the like), being strong against bending, being high in thermal conductivity and being inexpensive, Cu, Al and the like are preferred and Cu is especially preferred.

Although the thickness of the auxiliary electrode layer is not particularly limited, the range of 0.001 to 100 μm in a usual design specification, preferably 0.01 to 25 μm, is recommended. Although a known treatment method can be used for the formation of an auxiliary electrode, it is preferred to form the electrode by a sputtering method. Afterward, as necessary, the conductivity may be enhanced by performing electrolytic/electroless wet metal plating or the like to further make the film thickness thick.

Moreover, as necessary, for the purpose of the protection (mainly oxidation prevention) of the auxiliary electrode layer, a high melting point metal layer composed of Ni, Ni/Cr, Cr, Ti, Mo and the like and an oxide layer composed of oxides thereof may be disposed as upper and lower layers of the auxiliary electrode layer.

The electroconductive laminate of the present invention is characterized in that it is substantially free of a resin component that may volatilize during heat treatment of the electroconductive laminate carried out at 130° C. for 2 hours. The wording “substantially free of” means that an abundance is in the range from 0 to 20,000, when using 6890N and 5975MSD manufactured by Agilent, and PY-2020iD manufactured by Frontier Lab as a measuring instrument, a measurement condition of gas chromatography is that temperature range is 40 to 130° C., temperature rising speed is 0.8° C./min, the temperature in the furnace of a pyrolyzer is 130° C., a temperature condition of an interface is 200° C., and a volatile composition other than a volatile substance of a solvent and a volatile substance based on initiator is determined along the following criteria. In this case, the electroconductive laminate has a hard coat layer, as well as is in a state where the necessary all layers is formed on a polycarbonate substrate.

With regard to the electroconductive laminate of the present invention, a total content of organic compounds containing a sulfur element contained therein is preferably 0 to 2,000 ppm, and more preferably 0 to 500 ppm. An organic compound containing a sulfur element is used such as a catalyst. The phrase “a total content of an organic compound containing sulfur element” in the present invention means a total content of such organic compounds. A measurement of the content of an organic compound containing a sulfur element is performed by using an energy dispersive X-ray fluorescence spectrometer FDX-700HS (Shimadzu), where the measurement includes preparing a 50×50 mm size of the transparent electroconductive laminate, arranging the laminate on the sample plate such that the electrically conductive layer surface is irradiated with X-rays, preparing a calibration curve of sulfur by a quantitative analysis method, and measuring the sulfur content. When the total content of an organic compound containing a sulfur element exceeds 2,000 ppm, especially when the sulfur content is more than 500 ppm, a tendency of corrosion of the electrically conductive layer, i.e. such as an electrode is increase.

EXAMPLES

The present invention will be further explained in detail in accordance with the following examples, but it is not construed as limiting the present invention to these examples. In the examples, “part” and “%” are based on mass unless otherwise specified.

Production Example 1: Production of a Phenolic Novolac Acrylate (1)

In a reaction vessel equipped with a stirrer, a thermometer, a dropping funnel and a reflux apparatus, 150 g of phenol novolac resin (a weight average molecular weight of 700 to 900, an epoxy equivalent of 150 to 200) and 550 g of epichlorohydrin were mixed, and 110 g of an aqueous solution of sodium hydroxide (48.5%) was added dropwise for 2 hours under a temperature of 100° C. and a reduced pressure of 100 to 200 mmHg.

After the reaction was finished, a reaction temperature of the reaction mixture was lowered to a room temperature, and excess amounts of an aqueous solution of sodium hydroxide were neutralized with an acid, then the reaction mixture was heated under a reduced pressure to remove excess amounts of epichlorohydrin.

Next, the resulting reaction mixture was dissolved in methyl isobutyl ketone, and a salt of byproduct was removed by water filtration to obtain a solution of phenol novolac epoxy resin.

To the resulting phenol novolac epoxy resin (solid contents: 100 parts by mass), 1000 ppm of methoquinone (hydroquinone monomethylether) and 2000 ppm of triphenylphosphine were added, and acrylic acid was added dropwise under a temperature of 100° C. so as to an acid value of the resulting resin became not greater than 1 mg KOH/g, to obtain a phenolic novolac epoxy acrylate (1).

The obtained phenolic novolac epoxy acrylate (1) had a weight average molecular weight of 950, a hydroxyl value of 140 mgKOH/g and a refractive index of 1.572.

Production Example 2: Production of a Phenolic Novolac Acrylate (2)

In a reaction vessel equipped with a stirrer, a thermometer, a dropping funnel and a reflux apparatus, 150 g of phenol novolac resin (a weight average molecular weight of 900 to 1100, an epoxy equivalent of 150 to 200) and 550 g of epichlorohydrin were mixed, and 110 g of an aqueous solution of sodium hydroxide (48.5%) was added dropwise for 2 hours under a temperature of 100° C. and a reduced pressure of 100 to 200 mmHg. After the reaction was finished, a reaction temperature of the reaction mixture was lowered to a room temperature, and excess amounts of an aqueous solution of sodium hydroxide were neutralized with an acid, then the reaction mixture was heated under a reduced pressure to remove excess amounts of epichlorohydrin.

Next, the resulting reaction mixture was dissolved in methyl isobutyl ketone, and a salt of byproduct was removed by water filtration to obtain a solution of phenol novolac epoxy resin.

To the resulting phenol novolac epoxy resin (solid contents: 100 parts by mass), 1000 ppm of methoquinone (hydroquinone monomethylether) and 2000 ppm of triphenylphosphine were added, and acrylic acid was added dropwise under a temperature of 100° C. so as to an acid value of the resulting resin became not greater than 1 mg KOH/g, to obtain a phenolic novolac epoxy acrylate (2).

The obtained phenolic novolac epoxy acrylate (2) had a weight average molecular weight of 1200, a hydroxyl value of 137 mgKOH/g and a refractive index of 1.571.

Production Example 3: Production of Polyfunctional Urethane Acrylate

In a four-necked flask of 1 L equipped with a thermometer, a cooling tube, and a stirrer, 341 g of polycarbonate diol of 1,5-pentanediol and 1,6-hexanediol (manufactured by Asahi Kasei Chemicals Corporation, PCDL T-5652, number average molecular weight: 2000), 17 g of acrylic acid adduct of 1,6-hexanediol diglycidyl ether (manufactured by Showa Highpolymer, Ripoxy SP-16LDA), 43 g of isophorone diisocyanate, 0.2 g of dibutyltin dilaurate (reaction catalyst), and 400 g of methyl ethyl ketone (organic solvent) were added, and reaction was performed while stirring at 70° C. for 24 hours. After the reaction, it was confirmed that no isocyanate residue was observed by infrared absorption spectrum. As a result, unsaturated group-containing urethane resin (polyfunctional urethane acrylate) having 30,000 of a number-average molecular weight and a degree of unsaturation of 0.23 mol/kg was obtained. The obtained Polyfunctional urethane acrylate had three to four acrylate groups (average value) in one molecule.

Example 1

A hard coating composition was prepared by using the phenolic novolac epoxy acrylate (1) obtained by Production example 1 as a component (A), a bisphenol A ethylene oxide (2 mols)-modified diacrylate as a component (B), pentaerythritol triacrylate as a component (C), and a Polyfunctional urethane acrylate obtained in production example 3 as a component (D). Raw materials shown in Table 1 were mixed in the solid amounts shown in Table 1, and were stirred to obtain a hard coating composition.

The resulting hard coating composition was dropped on an optical PC film (trade name Pureace, manufactured by Teijin Limited, 100 μm) and was coated with a bar coater #9.

After the coating, the resulting coat was dried at 70° C. for one minute and was irradiated by ultraviolet rays of 350 mJ with a ultraviolet ray irradiator (manufactured by Fusion) to obtain a hard coat film composed of the polycarbonate film and a hard coat layer having a thickness of 5.0 μm.

The refractive index of the hard coat layer was measured by an Abbe's refractometer in conformity with JIS (Japanese Industrial Standard) K0062.

Examples 2-15

A hard coating composition was prepared in a same manner as in Example 1 except that a component and amounts as the compound (A) was changed as shown in Table 1, and amounts of the components (B) to (D) were changed as shown in Table 1. Using the resulting hard coating composition, a hard coat layer was formed in a same manner as in Example 1.

Comparative Examples 1-13

A hard coating composition was prepared in a same manner as in Example except that its content and composition ratio of a hard coating composition was changed as shown in Table 2. Using the resulting hard coating composition, a hard coat layer was formed in a same manner as in Example 1.

Example 16: Formation of Color Difference Adjusting Layer and Electrically Conducting Layer in Use of Hard Coating Compositions of Examples 1-15

A titanium oxide-containing dispersion (concentration of titanium oxide: 4 wt %) was obtained by adding isobutyl alcohol (i-BuOH) to a dispersion of ultrafine particles of titanium oxide (an average primary particle diameter: 30 nm) in n-butyl alcohol.

A solution of dipentaerythritol hexaacrylate in isobutyl alcohol (4 wt %) was prepared, which was a solution of UV curing resin component.

The titanium oxide-containing dispersion and the solution of UV curing resin component was added so as to obtain composition contents of titan oxide of 25 parts by mass and dipentaerythritol hexaacrylate of 75 parts by mass.

Next, a mixture ratio of the titanium oxide-containing dispersion and the solution of UV curing resin component was adjusted so as to minimize a difference (ΔR) of R1 and R2, wherein R1 is a reflectance where a light source having a wavelength in a range of 500 to 750 nm was irradiated to an electroconductive laminate, and R2 is a reflectance where a light source having a wavelength in a range of 500 to 750 nm was irradiated to an electroconductive laminate after immersing into a strong acid aqueous solution obtained by a mixing of 12 N hydrochloric acid, 16 N nitric acid and water in a mass ratio of 12 N hydrochloric acid:16 N nitric acid:water being 3.3:1.0:7.6, at a temperature of 40° C. for three minutes and dried, to obtain a composition for a color difference adjusting layer. The composition for a color difference adjusting layer contained 40 parts of titanium oxide based on 100 parts by mass of a curing resin.

The resultant composition for a color difference adjusting layer was dropped on each of the hard coat films obtained by the Examples 1-13 and was coated in use of a bar coater #3.

After the coating, the resulting coat was dried at 70° C. for one minute and was irradiated by ultraviolet rays of 350 mJ with a ultraviolet ray irradiator (manufactured by Fusion) to obtain a color difference adjusting layer on the hard coat layer.

On the resulting color difference adjusting layer, an ITO layer was formed by a sputtering method in use of indium oxide-tin oxide target with a density of arrangement of 98% containing indium oxide and tin oxide with a mass ratio of 95:5, to obtain an amorphous ITO layer. A thickness of the resulting ITO layer was about 30 nm, and a surface electrical resistance after formation of the layer was about 150 Ω/square.

In case of applying a color adjusting layer on each of a hard coat films obtained by the Examples 13 and 14, a color adjusting layer was applied with a change of an amount of titanium oxide based on 100 parts by mass of a curing resin shown in the Table below.

Comparative Example 14: Formation of Color Difference Adjusting Layer and Electrically Conducting Layer in Use of Hard Coating Compositions of Comparative Examples 1-13

On each of the hard coat films obtained by the Comparative Examples 1-13, a color difference adjusting layer was formed in a same manner of Example 16.

On the resulting color difference adjusting layer, an ITO layer was formed by a sputtering method in use of indium oxide-tin oxide target with a density of arrangement of 98% containing indium oxide and tin oxide with a mass ratio of 95:5, to form an ITO layer, which obtained a transparent electroconductive laminate as a movable electrode base plate.

A thickness of the resulting ITO layer was about 30 nm, and a surface electrical resistance after formation of the layer was about 150 Ω/square.

In comparative example 10, a color adjusting layer was applied with a change of an amount of titanium oxide based on 100 parts by mass of a curing resin shown in the Table below.

In use of hard coat films obtained by the Examples 1-15 and Comparative examples 1-13, and transparent electrically conducting layers obtained by the Example 16 and Comparative example 14, the tests described below were examined. Obtained test results were shown in Tables 1 and 2.

Measurement of a Reflectance Difference ΔR

A reflectance (R1) of the transparent electrically conducting layers obtained by the Example 16 and Comparative Example 14 were measured at an incident angle of 10 degrees with a spectrophotometer (U-3000, produced by Hitachi Ltd.) in conformity with JIS K5600-4-5.

A wavelength of the light source used in a measurement of the reflectance was in a range of 500 to 750 nm.

Then, the transparent electrically conducting layers obtained by the Examples and Comparative Examples were immersed into a strong acid aqueous solution obtained by a mixing of 12 N hydrochloric acid, 16 N nitric acid and water in a mass ratio of 12 N hydrochloric acid:16 N nitric acid:water being 3.3:1.0:7.6, at a temperature of 40° C. for three minutes and dried. To the treated transparent electrically conducting layers, a light source having a wavelength in a range of 500 to 750 nm was irradiated to measure a reflectance (R2). In the measurement, the reflectance (R1) means a reflectance where a transparent electrically conducting layer exists, as shown a part (13) in FIG. 1. The reflectance (R2) means a reflectance where a transparent electrically conducting layer does not exist, as shown a part (11) in FIG. 1.

A difference of R1 and R2 was referred to as ΔR. A maximum ΔR value within a wavelength range of 500 nm to 700 nm was shown in Tables 1 and 2.

Evaluation Method of Interference Fringes

On a polycarbonate substrate, each of the hard coating compositions obtained by the Examples 1-15 and Comparative examples 1-13 was applied in use of bar coater, then, the resulting coat was dried at 70° C. for one minute and was irradiated by Fusion-H light source, to obtain a test sample for the above examples and comparative examples.

The resultant test sample was affixed on a black acrylic plate with the size of 100 mm by 100 mm in use of an adhesive for optical film use to appear a hard coat layer of the test sample on the surface.

A stand-type three-wavelength fluorescent light (SLH-399 model manufactured by Twinbird Corporation) was placed, and the test sample was placed perpendicularly below the fluorescent light in the distance between the light and the test sample being 10 cm, then the test sample was visually observed and evaluated under the following evaluation criteria. As for a test sample having good evaluation result (∘), a visual observation under the sunlight was additionally performed.

∘∘: No interference fringes (interference pattern) are observed under either the three-wavelength fluorescent light or the sunlight.

∘: No interference fringes (interference pattern) are observed under the three-wavelength fluorescent light, however a slight interference fringes are observed under the sunlight.

Δ: Slight interference fringes (interference pattern) are observed.

x: Interference fringes (interference pattern) are clearly observed.

Evaluation of Etching Mark

The resultant transparent electroconductive laminates obtained by the Example 16 and Comparative example 14 were immersed into a strong acid aqueous solution at 40° C. for three minutes for etching treatment, wherein the strong acid aqueous solution was obtained by a mixing of 12 N hydrochloric acid, 16 N nitric acid and water in a mass ratio of 12 N hydrochloric acid:16 N nitric acid:pure water being 3.3:1.0:7.6, to perform patterning. Using resultant samples with patterning, a stand-type three-wavelength fluorescent light (SLH-399 model manufactured by Twinbird Corporation) was placed, and the test sample was placed perpendicularly below the fluorescent light in the distance between the light and the test sample being 10 cm, then the test sample was visually observed and evaluated under the following evaluation criteria. As for a test sample having good evaluation result (∘), a visual observation under the sunlight was additionally performed.

∘∘: Hardly differentiating between a patterned part and a non-patterned part under either the three-wavelength fluorescent light or the sunlight.

∘: Slightly differentiating between a patterned part and a non-patterned part under the sunlight, however hardly differentiating between a patterned part and a non-patterned part under the three-wavelength fluorescent light.

Δ: Slightly differentiating between a patterned part and a non-patterned part under the three-wavelength fluorescent light.

x: Clearly differentiating between a patterned part and a non-patterned part under the three-wavelength fluorescent light.

Method for Confirmation of the Presence or Absence of a Volatilization Resin Component

10 mg of the obtained transparent electroconductive laminate in Example 16 and Comparative Example 14, the measurement was performed under the following conditions.

A measuring instrument of 6890N and 5975MSD manufactured by Agilent and PY-2020iD manufactured by Frontier Lab were used. A measurement condition of gas chromatography was that temperature range was 40 to 130° C., temperature rising speed was 0.8° C./min, the temperature in the furnace of a pyrolyzer was 130° C., the temperature condition of an interface was 200° C. Also, a volatile composition other than a volatile substance based on a solvent and a volatile substance based on an initiator is determined along the following criteria.

∘: Abundance is in the range from 0 to 20,000

Δ: Abundance is in the range from 20,001 to 39,999

x: Abundance is greater than or equal to 40,000

Method for Measuring the Sulfur Content

The transparent electroconductive laminates obtained in Example 16 and Comparative Example 14 were prepared in 50×50 mm size, and each laminate was arranged on the sample plate such that an electrically conductive layer surface was irradiated with X-rays, and a measurement was performed undear the following condition. Energy-dispersive X-ray fluorescence analyzer EDX-700HS (manufactured by Shimadzu Corporation) was used as measurement equipment, preparing a calibration curve of sulfur by a quantitative analysis method, and sulfur content was determined in accordance the following criteria.

∘: Sulfur content is 0 to 100 ppm

Δ: Sulfur content is 101 to 500 ppm

x: Sulfur content is equal to or higher than 501 ppm

Method for Confirmation of Corrosion of an Auxiliary Electrode Layer

The transparent electroconductive laminates obtained in Example 16 and Comparative Example 14 were prepared in 50×50 mm size, and each laminate was arranged so as to laminate surface was contacted with the copper plate. Next, a stainless steel plate having a weight of 200 g was arranged, and 1 kg of weight was further placed thereon. In such a condition, the laminate was provided into a heat and humidity testing machine at 85° C.×85% RH. After 250 hours, the laminate was removed from the testing machine, and it was determined in accordance the following criteria.

∘: Discoloration of the copper plate cannot be confirmed

Δ: Discoloration of the copper plate was slightly confirmed

x: Discoloration of the copper plate was confirmed

Adhesion Evaluation 1 (Adhesion of Electroconductive Laminate)

The adhesion test was performed in accordance with JIS K5400. Each of the transparent electroconductive laminates obtained by the Example 16 and Comparative Example 14 was subjected to cross cutting so as to have 100 pieces of cut squares (grid pattern) with an area of 1 mm². Then, a cellophane pressure-sensitive adhesive tape was completely stuck on the prepared grid pattern and one end of the tape was pulled upward and peeled off. This peeling operation was performed three times on a same part. Afterward, the number of squares from which a part of the laminate was peeled off was judged according to the following criteria. Evaluating result “8” and more described below were determined to be acceptable.

10: There is no square from which a part of the laminate was peeled off.

8: There are not more than 5 squares from which a part of the laminate was peeled off.

6: There are more than 5 and not more than 15 squares from which a part of the laminate was peeled off.

4: There are more than 15 and not more than 35 squares from which a part of the laminate was peeled off.

2: There are more than 35 and not more than 65 squares from which a part of the laminate was peeled off.

0: There are more than 65 and not more than 100 squares from which a part of the laminate was peeled off.

Adhesion Evaluation 2 (Adhesion of Hard Coat Film)

The hard coat films obtained by the Examples 1-15 and Comparative examples 1-13 were immersed into ion exchanged water at 95-100° C. for 24 hours. After one hour had passed from immersion, cross cutting was subjected so as to have 100 pieces of cut squares (grid pattern) with an area of 1 mm². Then, a cellophane pressure-sensitive adhesive tape was completely stuck on the prepared grid pattern and one end of the tape was pulled upward and peeled off. This peeling operation was performed three times on a same part. Afterward, the number of squares from which a part of the laminate was peeled off was judged according to the above criteria with six-grade evaluation in the Adhesion evaluation 1.

Severe Adhesion Test

The hard coat films obtained by the Examples 1-15 and Comparative examples 1-13 were treated in a heat and humidity testing machine at 85° C.×85% RH for 500 hours. One hour after moist heat treatment, cross cutting was subjected so as to have 100 pieces of cut squares (grid pattern) with an area of 1 mm². Then, a cellophane pressure-sensitive adhesive tape was completely stuck on the prepared grid pattern and one end of the tape was pulled upward and peeled off. This peeling operation was performed three times on a same part. Afterward, the number of squares from which a part of the laminate was peeled off was judged according to the above criteria with six-grade evaluation in the Adhesion evaluation 1.

TABLE 1 Example 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 Hard coat layer Phenolic novolac epoxy acrylate (1) 15.00 25.00 20.00 20.00 20.00 20.00 20.00 20.00 15.00 25.00 20.00 20.00 20.00 20.00 Phenolic novolac epoxy acrylate (2) 20.00 Bisphenol A EO-modified (2 mol) 30.00 30.00 25.00 35.00 30.00 30.00 35.00 25.00 35.00 25.00 30.00 30.00 30.00 30.00 30.00 diacrylate Pentaerythritol triacrylate 30.00 30.00 30.00 30.00 25.00 35.00 25.00 35.00 25.00 35.00 30.00 30.00 30.00 30.00 30.00 Polyfunctional urethane acrylat 25.00 15.00 25.00 15.00 25.00 15.00 20.00 20.00 25.00 15.00 20.00 20.00 20.00 20.00 20.00 Bifunctional urethane acrylate(CN-9893) Sulfur catalyst-containing multi- functional acrylate Ethoxylated orthophenyl phenol acrylate High refractive index filler (zirconia: ZRMIBK30WT %) Irgacure 184 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00 5.00 Methyl isobutyl ketone 3.75 6.25 5.00 5.00 5.00 5.00 5.00 5.00 3.75 6.25 5.00 5.00 5.00 5.00 5.00 Isobutyl alcohol 78.75 78.75 78.75 78.75 78.75 78.75 78.75 78.75 78.75 78.75 78.75 78.75 78.75 78.75 78.75 Butyl acetate 75.00 72.50 73.75 73.75 73.75 73.75 73.75 73.75 75.00 72.50 73.75 73.75 73.75 73.75 73.75 Total amounts 262.50 262.50 262.50 262.50 262.50 262.50 262.50 262.50 262.50 262.50 262.50 262.50 262.50 262.50 262.50 Refractive index of hard coat layer 1.535 1.541 1.537 1.540 1.538 1.538 1.539 1.537 1.536 1.540 1.538 1.538 1.538 1.538 1.538 Layer thickness (μm) 3 3 3 3 3 3 3 3 3 3 3 5 3 3 3 Color An amount of ultrafine particles (parts 40 40 40 40 40 40 40 40 40 40 40 40 10 200 40 difference by mass) adjusting laye (Ex. 16) Evaluation ΔMax |R1 − R2| (%) (500-750) 0.63 0.62 0.71 0.59 0.71 0.68 0.65 0.54 0.73 0.59 0.73 0.60 0.81 0.95 0.64 Interference fringes (visual appearance ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ evaluation) Eching mark (visual evaluation) ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ Δ ◯ presence or absence of the volatile ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ resin component Sulfur content ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ Corrosion of auxiliary electrode layer ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ ◯ Adhesion evaluation 1 10 10 10 10 10 10 10 10 10 10 10 10 10 10 10 Adhesion evaluation 2 10 10 10 10 10 10 10 10 10 10 10 10 10 8 10 Severe adhesion test 10 10 10 10 10 10 10 10 10 10 10 10 10 8 10

TABLE 2 Comparative example 1 2 3 4 5 6 7 Hard coat layer Phenolic novolac epoxy acrylate (1) 35.00 5.00 20.00 20.00 20.00 Phenolic novolac epoxy acrylate (2) Bisphanol A EO-modified (2 mol) diacrylate 30.00 35.00 45.00 15.00 30.00 Pentaerythritol triacrylate 100.00 30.00 35.00 30.00 30.00 45.00 Polyfunctional urethane acrylat 5.00 25.00 5.00 35.00 5.00 Bifunctional urethane acrylate(CN-9893) Sulfur catalyst-containing multi-functional 100.00 acrylate Ethoxylated orthophenyl phenol acrylate High refractive index filler (zirconia: ZRMIBK30WT %) Irgacure 184 5.00 5.00 5.00 5.00 5.00 5.00 5.00 Methyl isobutyl ketone 0.00 0.00 8.75 1.25 5.00 5.00 5.00 Isobutyl alcohol 78.75 78.75 78.75 78.75 78.75 78.75 78.75 Butyl acetate 78.75 78.75 70.00 77.50 73.75 73.75 73.75 Total amounts 262.50 262.50 262.50 262.50 262.50 262.50 262.50 Refractive index of hard coat layer 1.520 1.524 1.540 1.530 1.543 1.534 1.539 Layer thickness (μm) 3 3 3 3 3 3 3 Color An amount of ultrafine particles (parts 40 40 40 40 40 40 40 difference by mass) adjusting laye (Com. 14) Evaluation ΔMax |R1 − R2| (%) (500-750) 2.41 2.63 0.64 1.56 1.26 1.42 0.61 Interference fringes (visual appearance X X ◯ X Δ X ◯ evaluation) Eching mark (visual evaluation) X X ◯ X Δ X ◯ presence or absence of the volatile resin ◯ ◯ ◯ ◯ ◯ ◯ ◯ component Sulfur content ◯ X ◯ ◯ ◯ ◯ ◯ Corrosion of auxiliary electrode layer ◯ X ◯ ◯ ◯ ◯ ◯ Adhesion evaluation 1 10 10 10 10 10 10 10 Adhesion evaluation 2 10 10 0 10 0 0 0 Severe adhesion test 10 10 0 10 0 0 0 Comparative example 8 9 10 11 12 13 Hard coat layer Phenolic novolac epoxy acrylate (1) 20.00 65.00 65.00 Phenolic novolac epoxy acrylate (2) Bisphanol A EO-modified (2 mol) diacrylate 30.00 Pentaerythritol triacrylate 15.00 15.00 15.00 40.00 28.00 Polyfunctional urethane acrylat 35.00 Bifunctional urethane acrylate(CN-9893) 70.00 60.00 42.00 Sulfur catalyst-containing multi-functional acrylate Ethoxylated orthophenyl phenol acrylate 20.00 20.00 High refractive index filler (zirconia: 30.00 30.00 ZRMIBK30WT %) Irgacure 184 5.00 5.00 5.00 5.00 5.00 5.00 Methyl isobutyl ketone 5.00 16.25 16.25 70.00 0.00 70.00 Isobutyl alcohol 78.75 88.75 88.75 113.75 78.75 78.75 Butyl acetate 73.75 72.50 72.50 43.75 78.75 8.75 Total amounts 262.50 282.50 282.50 332.50 262.50 262.50 Refractive index of hard coat layer 1.537 1.569 1.569 1.570 1.510 1.569 Layer thickness (μm) 3 3 3 3 3 3 Color An amount of ultrafine particles (parts 40 40 300 40 40 40 difference by mass) adjusting laye (Com. 14) Evaluation ΔMax |R1 − R2| (%) (500-750) 0.71 0.52 1.41 2.35 2.41 2.47 Interference fringes (visual appearance ◯ ⊚ ◯ X X X evaluation) Eching mark (visual evaluation) ◯ ⊚ Δ X X X presence or absence of the volatile resin ◯ Δ Δ ◯ ◯ ◯ component Sulfur content ◯ ◯ ◯ ◯ ◯ ◯ Corrosion of auxiliary electrode layer ◯ ◯ ◯ ◯ ◯ ◯ Adhesion evaluation 1 10 10 4 10 10 10 Adhesion evaluation 2 0 0 0 10 10 10 Severe adhesion test 0 0 0 10 10 10

In the Tables 1 and 2, each term means as follows.

IRGACURE-184: 1-hydroxycyclohexyl phenyl ketone, a photoinitiator.

Bisphenol A EO-modified (2 mol) diacrylate: Aronix M-211B manufactured by Toa gosei Co., Ltd., bisphenol A ethyleneoxide-modified (2 mol) diacrylate having 4 mols of ethylene oxide structure in the molecule.

High refractive index filler 1: zirconia: ZRMIBK30 WT %, zirconium oxide, manufactured by CIK NanoTec.

Bifunctional urethane acrylate: NV (non-volatile component) 100, CN-9893 manufactured by Sartomer Corp.

Each of the hard coat films having the hard coat layer obtained by applying the hard coating composition of Examples had high refractive index and excellent hardness without interference fringes. In addition, the resultant hard coat films had excellent elongation and bending resistance, furthermore, had no problem about initial adhesion properties, adhesion property as a hard coat film, and severe adhesion evaluations. The content of a volatile resin component of the electroconductive laminate and sulfur content were small, and corrosion problems of the electroconductive layer were not occurred.

Comparative example 1 was a comparative example in which conventional hard coat layer was formed. In the Comparative example 1, interference fringes were observed derived from low refractive index. Comparative example 2 was a comparative example in which a sulfur-catalyst-containing polyfunctional acrylate was used. In the Comparative example 2, sulfur content is large and corrosion of the auxiliary electrode layer was observed. Comparative examples 3 and 4 were a comparative example in which an amount of the component (A) was out of the scope of claimed invention of the present application. When the amount was less than the range of the claimed invention (Comparative examples 4), refractive index lowered and there was a disadvantage that defect of interference fringes occurred. When the amount was more than the range of the claimed invention (Comparative example 3), there was a disadvantage that defects of inferior adhesion property occurred.

Comparative examples 5 and 6 were a comparative example in which an amount of the component (B) was out of the scope of claimed invention of the present application. In the comparative examples, when the amount was less than the range of the claimed invention, defects of refractive index was lowered and interference fringes occurred. When the amount was more than the range of the claimed invention, defects of inferior hardness and adhesion property occurred.

Comparative examples 7 and 8 were a comparative example in which an amount of the component (C) was out of the scope of claimed invention of the present application. In the comparative examples, when the amount was less than the range of the claimed invention, defects of refractive index was lowered and interference fringes occurred. When the amount was more than the range of the claimed invention, defects of inferior hardness occurred.

Comparative examples 9 and 10 were comparative examples in which ethoxylated ortho-phenylphenol acrylate which causes a generation of a volatilization resin was formulated, in place of the component (B). In Comparative Example 10 was a comparative example in which it contains a large amount of ultrafine particles in the color difference adjustment layer. In both examples, there are many volatilization resin component. In comparative Example 10, an etching mark also exists, and adhesion property became worse.

Comparative examples 11 and 13 were comparative examples in which a bifunctional urethane acrylate was used in order to provide an elongation to a hard coat layer. Also, Comparative examples 11 and 13 included high refractive index fillers. In these comparative examples including high refractive index fillers provided indeed a high refractive index of the obtaining hard coat layer. On the other hand, each the obtaining hard coat layer of the comparative examples was observed appearance of interference fringes. The reason why the comparative examples had appearance of interference fringes seems to be a mixture of resin components having lower refractive indexes which form an hard coat layer and high refractive index fillers which exist between the resin components. The constitution seems to provide inferior prevention of appearance of interference fringes because of a bad influence of the resin components' lower refractive indexes, even if a refractive index itself of a hard coat layer is high.

Comparative Example 12 was a comparative example in which extensible and hardness of the hard coat layer is equivalent to the embodiment, but the refractive index is lower cases. From this comparative example 12, in order to suppress the two of etching mark and the interference fringes, it will be understood that an adjustment of refractive index in the resin system and high extensibility are required.

From the results of Examples and Comparative Examples, it is understand that the hard coat layer obtained by the present invention shows an excellent interference fringe suppression effect, and an adhesion effect is achieved.

INDUSTRIAL APPLICABILITY

The present invention provides a hard coat layer having stretchability and excellent adhesion property toward a polycarbonate substrate, as well as high visibility and excellent hardness. The transparent hard coat layer obtainable by using the hard coating composition according to the present invention has features of high refractive index. Therefore, the present invention has an advantage such as excellent stretchability without interference fringes in case that the hard coat layer according to the present invention is applied onto a high refractive index substrate film such as a polycarbonate film. In addition, it is able to withstand in the severe adhesion test, and the application to be used has spread significantly.

DESCRIPTION OF THE REFERENCE NUMERALS

-   1: a polycarbonate substrate, -   3: a hard coat layer, -   5: a color difference adjusting layer, -   7: an electrically conducting layer, -   10: an electroconductive laminate, -   11: a part where a reflectance R2 shows, and -   13: a part where a reflectance R1 shows. 

What is claimed is:
 1. An electroconductive laminate in which a hard coat layer and an electrically conducting layer are formed on at least one surface of a polycarbonate substrate, wherein the hard coat layer is obtained by a hard coating composition comprising (A) a phenolic novolac acrylate having two or more acrylate groups, (B) a bisphenol structure-containing diacrylate having 2 to 4 moles of alkylene oxide structure with two or three carbon atoms in each molecule, (C) a polyfunctional acrylate having three or more acrylate groups, and (D) a polyfunctional urethane acrylate having three or more acrylate groups and an ester structure, wherein the hard coating composition comprises 15 to 25 parts by mass of the phenolic novolac acrylate (A), 25 to 35 parts by mass of the bisphenol structure-containing diacrylate (B), 25 to 35 parts by mass of the polyfunctional acrylate (C), and 15 to 25 parts by mass of the polyfunctional urethane acrylate (D), with respect to 100 parts by mass of a resin content in the hard coating composition, and wherein the electroconductive laminate is substantially free of a resin component that may volatilize during heat treatment of the electroconductive laminate carried out at 130° C. for 2 hours.
 2. The electroconductive laminate according to claim 1, wherein the phenolic novolac acrylate (A) is represented by the following formula (I):

wherein R¹ represents H or CH₂OH, R² represents H or OH, n represents a number of 2 to 5 and m represents a number of 0 to
 5. 3. The electroconductive laminate according to claim 1, wherein the hard coat layer has a refractive index within a range of 1.535 to 1.545.
 4. The electroconductive laminate according to claim 1, wherein a total content of ZnO, TiO₂, CeO₂, SnO₂, ZrO₂ and indium tin oxide in the hard coat layer is less than or equal to 0.0001% by mass.
 5. The electroconductive laminate according to claim 1, wherein the electrically conducting layer has a thickness within a range of 5 to 100 nm.
 6. An electroconductive laminate in which a hard coat layer, a color difference adjusting layer, and an electrically conducting layer are formed on at least one surface of a polycarbonate substrate, wherein the hard coat layer is obtained by a hard coating composition comprising (A) a phenolic novolac acrylate having two or more acrylate groups, (B) a bisphenol structure-containing diacrylate having 2 to 4 moles of alkylene oxide structure with two or three carbon atoms in each molecule, (C) a polyfunctional acrylate having three or more acrylate groups, and (D) a polyfunctional urethane acrylate having three or more acrylate groups and an ester structure, wherein the hard coating composition comprises 15 to 25 parts by mass of the phenolic novolac acrylate (A), 25 to 35 parts by mass of the bisphenol structure-containing diacrylate (B), 25 to 35 parts by mass of the polyfunctional acrylate (C), and 15 to 25 parts by mass of the polyfunctional urethane acrylate (D), with respect to 100 parts by mass of a resin content in the hard coating composition, wherein the electroconductive laminate is substantially free of the resin component that may volatilize during a heat treatment of the electroconductive laminate carried out at 130° C. for 2 hours, wherein the color difference adjusting layer is obtained by a composition comprising a curing resin component (i), and at least one of metal oxide particles having an average primary particle diameter of 100 nm or less (ii) and metal fluoride particles having an average primary particle diameter of 100 nm or less (iii), and where a total mass of the particles (ii) and (iii) in the color difference adjusting layer is 1-200 parts by mass with respect to 100 parts by mass of the curing resin component (i), and wherein a difference ΔR of R1 and R2 is equal to or less than 1, wherein R1 is a reflectance obtained by irradiation with a light source having a wavelength in a range of 500 to 750 nm toward the electroconductive laminate, and R2 is a reflectance obtained by irradiation with a light source having a wavelength in a range of 500 to 750 nm toward an electroconductive laminate after immersion into a strong acid aqueous solution at 40° C. for three minutes and dried, wherein the strong acid aqueous solution is obtained by a mixing of 12 N hydrochloric acid, 16 N nitric acid and water in a mass ratio of 12 N hydrochloric acid:16 N nitric acid:water being 3.3:1.0:7.6.
 7. The electroconductive laminate according to claim 1, wherein a total content of a sulfur-containing organic compound in the electroconductive laminate is within a range of 0 to 2000 ppm.
 8. The electroconductive laminate according to claim 1, wherein the electroconductive laminate has an auxiliary electrode layer formed on the electrically conducting layer, and wherein a total thickness of the electrically conducting layer and the auxiliary electrode layer is within a range of 20 to 500 nm.
 9. The electroconductive laminate according to claim 1, in which a hard coat layer, a color difference adjusting layer, and an electrically conducting layer are formed on at least one surface of a polycarbonate substrate, and in which an anti-blocking layer obtained by a composition for forming an anti-blocking layer comprising a first component and a second component is formed on another surface of the transparent polycarbonate substrate, wherein the first component contains an acrylic copolymer having an unsaturated double bond, the second component contains a polyfunctional acrylate, a difference of SP values (ΔSP) of the first component (SP1) and the second component (SP2) is within a range of 1 to 2, and the anti-blocking layer having a microscopic convexoconcave on its surface is obtained by a phase separation that occurs between the first component and the second component after the composition for forming an antiblocking layer is applied.
 10. A touch panel having an electrode substrate on which an electrically conductive layer is formed on at least one surface of the electrode substrate, wherein the electroconductive laminate according to claim 1 is used as at least one electrode substrate.
 11. The electroconductive laminate according to claim 6, wherein a total content of a sulfur-containing organic compound in the electroconductive laminate is within a range of 0 to 2000 ppm.
 12. The electroconductive laminate according to claim 6, wherein the electroconductive laminate has an auxiliary electrode layer formed on the electrically conducting layer, and wherein a total thickness of the electrically conducting layer and the auxiliary electrode layer is within a range of 20 to 500 nm.
 13. The electroconductive laminate according to claim 6, in which a hard coat layer, a color difference adjusting layer, and an electrically conducting layer are formed on at least one surface of a polycarbonate substrate, and in which an anti-blocking layer obtained by a composition for forming an anti-blocking layer comprising a first component and a second component is formed on another surface of the transparent polycarbonate substrate, wherein the first component contains an acrylic copolymer having an unsaturated double bond, the second component contains a polyfunctional acrylate, a difference of SP values (ΔSP) of the first component (SP1) and the second component (SP2) is within a range of 1 to 2, and the anti-blocking layer having a microscopic convexoconcave on its surface is obtained by a phase separation that occurs between the first component and the second component after the composition for forming an antiblocking layer is applied.
 14. A touch panel having an electrode substrate on which an electrically conductive layer is formed on at least one surface of the electrode substrate, wherein the electroconductive laminate according to claim 6 is used as at least one electrode substrate. 